Technical Discussions
T.j
Engineering,
China, Joined Feb 2007, 2

T.j

Engineering,
China,
Joined Feb 2007
2
07:54 May-25-2007
How to inspect the rings with UT

hello,Does anyone know how to inspect the forge rings with UT,sometimes we found the cracks on the inner surface or on the port, and the surface is rough, so we can't use MPI or LPI, your advise would be highly appreciated. thank you!


 
 Reply 
 
Dave
Dave
05:40 May-29-2007
Re: How to inspect the rings with UT
I assume they are quite large steel rings, check out ASTM A388, surface finish is very important for UT. Rings and hollow forgings should be examined with straight beam and angle beam probes (angles, scan surfaces depend on size).
reference blocks with flat bottom holes and notches are usually required although DGS is also allowed in some cases.
If the surface is scaled you have to remove but if the surface has forging die marks you will have to get it machined to gat any useful results from UT. A388 recommends you not exceed 250micro inch unless agreed before hand.
As with many NDT methods, surface finish is critical for a good result.

----------- Start Original Message -----------
: hello,Does anyone know how to inspect the forge rings with UT,sometimes we found the cracks on the inner surface or on the port, and the surface is rough, so we can't use MPI or LPI, your advise would be highly appreciated. thank you!
------------ End Original Message ------------




 
 Reply 
 
Joe Buckley
Consultant, ASNT L-III, Honorary Secretary of BINDT
Level X NDT, BINDT, United Kingdom, Joined Oct 1999, 524

Joe Buckley

Consultant, ASNT L-III, Honorary Secretary of BINDT
Level X NDT, BINDT,
United Kingdom,
Joined Oct 1999
524
03:15 May-29-2007
Re: How to inspect the rings with UT
Depending on the Geometry/access you may find eddy current with an Orthogonal coil probe (as used for weld inspection) worth a try - It is quite tolerant of poor surface finish and or mild scaling

Joe

----------- Start Original Message -----------
: I assume they are quite large steel rings, check out ASTM A388, surface finish is very important for UT. Rings and hollow forgings should be examined with straight beam and angle beam probes (angles, scan surfaces depend on size).
: reference blocks with flat bottom holes and notches are usually required although DGS is also allowed in some cases.
: If the surface is scaled you have to remove but if the surface has forging die marks you will have to get it machined to gat any useful results from UT. A388 recommends you not exceed 250micro inch unless agreed before hand.
: As with many NDT methods, surface finish is critical for a good result.
: : hello,Does anyone know how to inspect the forge rings with UT,sometimes we found the cracks onthe inner surface or on the port, and the surface is rough, so we can't use MPI or LPI, your advise would be highly appreciated. thank you!
------------ End Original Message ------------




 
 Reply 
 
T.j
T.j
02:16 May-30-2007
Re: How to inspect the rings with UT
Thank you for your advise,you are right,they are quite large forge rings,the diameter of inner ring is about 1400mm,and the diameter of outer ring is about 1500mm.we would test with UT when we receiving them,
Before we didn't test them, but we found cracks near the surface about 3mm after we machined them.OK
i will check out ASTM A388.
thank you very much~


----------- Start Original Message -----------
: I assume they are quite large steel rings, check out ASTM A388, surface finish is very important for UT. Rings and hollow forgings should be examined with straight beam and angle beam probes (angles, scan surfaces depend on size).
: reference blocks with flat bottom holes and notches are usually required although DGS is also allowed in some cases.
: If the surface is scaled you have to remove but if the surface has forging die marks you will have to get it machined to gat any useful results from UT. A388 recommends you not exceed 250micro inch unless agreed before hand.
: As with many NDT methods, surface finish is critical for a good result.
: : hello,Does anyone know how to inspect the forge rings with UT,sometimes we found the cracks on the inner surface or on the port, and the surface is rough, so we can't use MPI or LPI, your advise would be highly appreciated. thank you!
------------ End Original Message ------------




 
 Reply 
 

Product Spotlight

Lyft™: Pulsed Eddy Current Reinvented

PEC Reinvented—CUI Programs Redefined Corrosion under insulation (CUI) is possibly the greatest u
...
nresolved asset integrity problem in the industry. Current methods for measuring wall thickness with liftoff, without removing insulation, all have severe limitations. Eddyfi introduces Lyft — a reinvented, high-performance pulsed eddy current (PEC) solution. The patent- pending system features a state-of-the-art portable instrument, real- time C-scan imaging, fast data acquisition with grid-mapping and dynamic scanning modes, and flexibility with long cables. It can also scan through thick metal and insulation, as well as aluminum, stainless steel, and galvanized steel weather jackets. Who else but Eddyfi to reinvent an eddy current technique and redefine CUI programs. Got Lyft?
>

YXLON Cougar EVO

Scalable small footprint X-ray inspection systems for assembly and laboratory applications. The
...
YXLON Cougar EVO series was designed to provide the "best-in- class" inspection solutions for SMT, semiconductor, and laboratory assembly applications, while maintaining a small system footprint for maximum convenience. With optimized software and hardware, these systems produce higher quality and more consistent results than other electronics inspection systems currently on the market.
>

GUL QSR1® Scanning

How do you measure pipe wall thickness without direct access to the area? QSR® Scanning - Guide Wav
...
e Quantitative Short Range Scanning.
>

SITEX CPSERIES

Teledyne ICM’s CPSERIES has been designed with a view to revolutionizing the handling and perfor
...
mances of portable X-Ray sets. Despite having managed to halve the weight of similar portable X-Ray generators available on the market (while continuing to provide the same power output), the SITEX CPSERIES generators feature a shutter, a laser pointer, a beryllium window, an aluminum filter and two integrated diaphragms (customized sizes are available upon request). Without compromising the robustness and reliability for which ICM products are renowned, the small size and light weight of the SITEX CPSERIES will radically change the way that you perform your RT inspections. And you will see a positive impact in terms of both quality and return on investment (ROI).
>