Bahram Hosseini
Director,
IQSecc, Iran, Joined Oct 2002, 4

Bahram Hosseini

Director,
IQSecc,
Iran,
Joined Oct 2002
4
00:34 Jul-10-2007
Root Pass Evaluation S.S. Pipes

Hi everybody,

Is there any NDT method (or idea) for evaluation of the root pass of austenitic stainless steel pipes which are suspected to use of the wrong electrode (i.e. E6010)?
The thickness range is from 5 to 20 mm. with variable diameter.

Regards,


B. Hosseini



 
 Reply 
 
Ryan Burns
Ryan Burns
03:30 Jul-10-2007
Re: Root Pass Evaluation S.S. Pipes
If weld prep angle allows, use of a XRF (Positive Material Analysis ie Niton) unit should work. For thickness closer to the 5mm mark, a smaller than standard head would likely have to be used. If you truly suspect E6010 was used (or another ferromagnetic rod) why not just use a small magnet?

Regards

Ryan.


----------- Start Original Message -----------
: Hi everybody,
: Is there any NDT method (or idea) for evaluation of the root pass of austenitic stainless steel pipes which are suspected to use of the wrong electrode (i.e. E6010)?
: The thickness range is from 5 to 20 mm. with variable diameter.
: Regards,
:
: B. Hosseini
------------ End Original Message ------------




 
 Reply 
 
Ryan Burns
Ryan Burns
05:14 Jul-11-2007
Re: Root Pass Evaluation S.S. Pipes
My preceding remarks are assuming just root pass is welded. If fill and cap are complete as well, then I am not sure. I found someone else with a similar problem, the thread can be viewed here.

Ryan.

----------- Start Original Message -----------
: If weld prep angle allows, use of a XRF (Positive Material Analysis ie Niton) unit should work. For thickness closer to the 5mm mark, a smaller than standard head would likely have to be used. If you truly suspect E6010 was used (or another ferromagnetic rod) why not just use a small magnet?
: Regards
: Ryan.
:
: : Hi everybody,
: : Is there any NDT method (or idea) for evaluation of the root pass of austenitic stainless steel pipes which are suspected to use of the wrong electrode (i.e. E6010)?
: : The thickness range is from 5 to 20 mm. with variable diameter.
: : Regards,
: :
: : B. Hosseini
------------ End Original Message ------------




 
 Reply 
 
Ryan Burns
Ryan Burns
05:17 Jul-11-2007
Re: Root Pass Evaluation S.S. Pipes
http://www.aws.org/cgi-bin/mwf/topic_show.pl?pid=65571;hl=


----------- Start Original Message -----------
: My preceding remarks are assuming just root pass is welded. If fill and cap are complete as well, then I am not sure. I found someone else with a similar problem, the thread can be viewed here.
: Ryan.
: : If weld prep angle allows, use of a XRF (Positive Material Analysis ie Niton) unit should work. For thickness closer to the 5mm mark, a smaller than standard head would likely have to be used. If you truly suspect E6010 was used (or another ferromagnetic rod) why not just use a small magnet?
: : Regards
: : Ryan.
: :
: : : Hi everybody,
: : : Is there any NDT method (or idea) for evaluation of the root pass of austenitic stainless steel pipes which are suspected to use of the wrong electrode (i.e. E6010)?
: : : The thickness range is from 5 to 20 mm. with variable diameter.
: : : Regards,
: : :
: : : B. Hosseini
------------ End Original Message ------------




 
 Reply 
 
Godfrey Hands
Consultant,
PRI Nadcap, United Kingdom, Joined Nov 1998, 304

Godfrey Hands

Consultant,
PRI Nadcap,
United Kingdom,
Joined Nov 1998
304
08:43 Jul-11-2007
Re: Root Pass Evaluation S.S. Pipes
----------- Start Original Message -----------
: Hi everybody,
: Is there any NDT method (or idea) for evaluation of the root pass of austenitic stainless steel pipes which are suspected to use of the wrong electrode (i.e. E6010)?
: The thickness range is from 5 to 20 mm. with variable diameter.
: Regards,
:
: B. Hosseini
------------ End Original Message ------------
Hi Barham (and Ryan).
I have come accross this problem a couple of times in the past, and we have been able to get a satisfactory solution.

Let us assume that the problem is caused mostly on closer welds and repairs where it is difficult for the welder to purde the line before welding.
If you can agree with this, then you only have these welds to inspect, otherwise its probably a 100% inspection regime.

We used (electro)magnetic methods as follows:
For thicknesses below 5.5 mm we used a hand held small magnet. test pieces needed to calibrate against.

For thicknesses between 5mm and about 11mm we used a permeability meter (Forster sell one but it is very expensive. Other companies also sell them for much less money). Again calibration pieces needed.

For thicknesses above 11 mm we used a multi-frequency eddy current instrument (in our cases we used IBG Eddyliner with 25mm diameter probe, which tests simultaneously at up to 8 frequencies. Frome memory, frequencies around 150 Hz seemed to work best, but other frequencies also contribute to the result).
Again calibration pieces are needed.

Please note. Depending on the pipe orientation (horizontal or vertical pipe), there will be different amounts of free ferrite in the weld from the heating effect of the welding. This is also true for repairs where extra heat has been introduced, so free ferrite in the weld will be higher.
Also if the weld is TIG root and stick filled, this will be different to TIG root and TIG fill and cap.

Looks like you have a major job on your hands.

Success.

Regards,

Godfrey Hands




 
 Reply 
 
B. Hosseini
Director,
IQSecc, Iran, Joined Oct 2002, 4

B. Hosseini

Director,
IQSecc,
Iran,
Joined Oct 2002
4
00:40 Jul-11-2007
Re: Root Pass Evaluation S.S. Pipes
Hi Ryan.
for using the magnet, there is no access to pipes inside, all Tie-in welds have already done.

B. Hosseini
----------- Start Original Message -----------
: If weld prep angle allows, use of a XRF (Positive Material Analysis ie Niton) unit should work. For thickness closer to the 5mm mark, a smaller than standard head would likely have to be used. If you truly suspect E6010 was used (or another ferromagnetic rod) why not just use a small magnet?
: Regards
: Ryan.
:
: : Hi everybody,
: : Is there any NDT method (or idea) for evaluation of the root pass of austenitic stainless steel pipes which are suspected to use of the wrong electrode (i.e. E6010)?
: : The thickness range is from 5 to 20 mm. with variable diameter.
: : Regards,
: :
: : B. Hosseini
------------ End Original Message ------------




 
 Reply 
 
Ingo Becker
Engineering, NDT Inspector & Sales
ec-works GmbH, Germany, Joined Apr 2000, 30

Ingo Becker

Engineering, NDT Inspector & Sales
ec-works GmbH,
Germany,
Joined Apr 2000
30
08:57 Jul-12-2007
Re: Root Pass Evaluation S.S. Pipes
It should also work with the use of eddy current. The electrical conductivities of the different electrode materials are different, and the eddy current method requires these conductivity differences. We have done exactly these inspection or search task several times. Please contact me for detailed information.

Best regards

Ingo Becker

----------- Start Original Message -----------
: Hi everybody,
: Is there any NDT method (or idea) for evaluation of the root pass of austenitic stainless steel pipes which are suspected to use of the wrong electrode (i.e. E6010)?
: The thickness range is from 5 to 20 mm. with variable diameter.
: Regards,
:
: B. Hosseini
------------ End Original Message ------------




 
 Reply 
 

Product Spotlight

EKOSCAN Phased Array

In order to always fit your needs, EKOSCAN can manufacture any type of UT transducer, either convent
...
ional or Phased Array. As an ISO 9001: 2015 certified company, EKOSCAN is extremely careful as far a material selection and manufacturing processes are concerned. Our probes guarantee our customers the benefits of latest innovations regarding piezo-composite, backing, impedance adaptation layer, etc. Specific probes for hostile environment: high temperature, high pressure, corrosive environment,etc. Specific probes designed to fit your specific application: optimization of every parameter to guarantee you the best detection.
>

NDTkit RT

NDTkit RT, TESTIA's Digital Radiography software The NDTkit product line software for X-ray analysi
...
s. NDTkit RT is a software benefiting from the Ultis kernel which is dedicated to radiographic image analysis. It offers a set of tools and filtering processes to assist RT operators in finding relevant flaws.
>

CIVA 2020 UT Module

CIVA NDE Simulation Software is the world leader of NDT Simulation. The UT simulation Module incl
...
udes: - "Beam computation": Beam propagation simulation - "Inspection Simulation": Beam interaction with flaws or specimens The user can simulate a whole inspection process (pulse echo, tandem or TOFD) with a wide range of probes (conventional, Phased- arrays or EMAT), components, and flaws.
>

Ultrasonic tomograph for imaging of concrete structures А1040 MIRA

Applicable for concrete inspection allowing imaging of the internal structure of objects from conc
...
rete, reinforced concrete, different stones. The operation applies pulse-echo technique at one-side access to the object. The instrument is feasible for concrete inspection for searching conduct ducts, conduits, detection of foreign inclusions, holes, honeycombing, cracks and other concrete defects.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window