Technical Discussions
azmi
azmi
01:21 Jul-04-2007
UT after MT. Surface preparation

Does it enough to perform UT after MT with manual cleaning on surface after MT? What i mean, UT still can be performed eventhough the weld surface is not cleaned by power brush.


 
 Reply 
 
chris s
chris s
08:00 Jul-06-2007
Re: UT after MT. Surface preparation
----------- Start Original Message -----------
: Does it enough to perform UT after MT with manual cleaning on surface after MT? What i mean, UT still can be performed eventhough the weld surface is not cleaned by power brush.
------------ End Original Message ------------

that should be fine. you will have problems if you ut and then mag. the ut gel will need to be completely removed.


 
 Reply 
 
Nigel Armstrong
Engineering, - Specialist services
United Kingdom, Joined Oct 2000, 1096

Nigel Armstrong

Engineering, - Specialist services
United Kingdom,
Joined Oct 2000
1096
06:33 Jul-11-2007
Re: UT after MT. Surface preparation
It depends on the overall condition of the scan surface(s). If such surfaces were very clean, smooth and free of spatter and other surface irregularities, then the MPI technician will only have needed to apply a very fine and even thickness contrast coating prior to MPI. This would make UT on the painted surface possible if the contast coat is tightly adhering and very thin. However if the surface condition was poor at the time of MPI, then you can expect a much thicker, less even thickness coating - MOPI techs tend to spray contrast coating until it looks a good smooth finish. My general advice would be to power brush the scanning surfaces prior to MPI because this allows the technician(s) more control over both the MPI (thinner more even coating) and the UT ( better probe coupling and manipulation) leading to a higher probability of detection of defects.


----------- Start Original Message -----------
: : Does it enough to perform UT after MT with manual cleaning on surface after MT? What i mean, UT still can be performed eventhough the weld surface is not cleaned by power brush.
: that should be fine. you will have problems if you ut and then mag. the ut gel will need to be completely removed.
------------ End Original Message ------------




 
 Reply 
 
chris s
chris s
00:18 Jul-12-2007
Re: UT after MT. Surface preparation
----------- Start Original Message -----------
: It depends on the overall condition of the scan surface(s). If such surfaces were very clean, smooth and free of spatter and other surface irregularities, then the MPI technician will only have needed to apply a very fine and even thickness contrast coating prior to MPI. This would make UT on the painted surface possible if the contast coat is tightly adhering and very thin. However if the surface condition was poor at the time of MPI, then you can expect a much thicker, less even thickness coating - MOPI techs tend to spray contrast coating until it looks a good smooth finish. My general advice would be to power brush the scanning surfaces prior to MPI because this allows the technician(s) more control over both the MPI (thinner more even coating) and the UT ( better probe coupling and manipulation) leading to a higher probability of detection of defects.
:
: : : Does it enough to perform UT after MT with manual cleaning on surface after MT? What imean, UT still can be performed eventhough the weld surface is not cleaned by power brush.
: : that should be fine. you will have problems if you ut and then mag. the ut gel will need to be completely removed.
------------ End Original Message ------------

i did not see any mention of a paint coating



 
 Reply 
 
Nigel Armstrong
Engineering, - Specialist services
United Kingdom, Joined Oct 2000, 1096

Nigel Armstrong

Engineering, - Specialist services
United Kingdom,
Joined Oct 2000
1096
05:33 Jul-13-2007
Re: UT after MT. Surface preparation
chris

If a fluorescent technique not requiring a contrast paint coating is required, then surface condition is even more critical. In nearly all other cases a contrast paint coat is required.

----------- Start Original Message -----------
: : It depends on the overall condition of the scan surface(s). If such surfaces were very clean, smooth and free of spatter and other surface irregularities, then the MPI technician will only have needed to apply a very fine and even thickness contrast coating prior to MPI. This would make UT on the painted surface possible if the contast coat is tightly adhering and very thin. However if the surface condition was poor at the time of MPI, then you can expect a much thicker, less even thickness coating - MOPI techs tend to spray contrast coating until it looks a good smooth finish. My general advice would be to power brush the scanning surfaces prior to MPI because this allows the technician(s) more control over both the MPI (thinner more even coating) and the UT ( better probe coupling and manipulation) leading to a higher probability of detection of defects.
: :
: : : : Does it enough to perform UT after MT with manual cleaning on surface after MT? What i mean, UT still can be performed eventhough the weld surface is not cleaned by power brush.
: : : that should be fine. you will have problems if you ut and then mag. the ut gel will need to be completely removed.
: i did not see any mention of a paint coating
------------ End Original Message ------------




 
 Reply 
 
chris s
chris s
08:09 Jul-17-2007
Re: UT after MT. Surface preparation
----------- Start Original Message -----------
are you talking about a developer?

: chris
: If a fluorescent technique not requiring a contrast paint coating is required, then surface condition is even more critical. In nearly all other cases a contrast paint coat is required.
: : : It depends on the overall condition of the scan surface(s). If such surfaces were very clean, smooth and free of spatter and other surface irregularities, then the MPI technician will only have needed to apply a very fine and even thickness contrast coating prior to MPI. This would make UT on the painted surface possible if the contast coat is tightly adhering and very thin. However if the surface condition was poor at the time of MPI, then you can expect a much thicker, less even thickness coating - MOPI techs tend to spray contrast coating until it looks a good smooth finish. My general advice would be to power brush the scanning surfaces prior to MPI because this allows the technician(s) more control over both the MPI (thinner more even coating) and the UT ( better probe coupling and manipulation) leading to a higher probability of detection of defects.
: : :
: : : : : Does it enough to perform UT after MT with manual cleaning on surface after MT? What i mean, UT still can be performed eventhough the weld surface is not cleaned by power brush.
: : : : that should be fine. you will have problems if you ut and then mag. the ut gel will need to be completely removed.
: : i did not see any mention of a paint coating
------------ End Original Message ------------




 
 Reply 
 

Product Spotlight

Conformable wedge transducer

The conformability is obtained with a flexible membrane filled with water between the transducer and
...
the inspected component. The coupling between the membrane and the component requires a small quantity of water or couplant. The conformable wedge combines the acoustic performance of immersion technique with good coupling and low attenuation.
>

CIVA 2020 UT Module

CIVA NDE Simulation Software is the world leader of NDT Simulation. The UT simulation Module incl
...
udes: - "Beam computation": Beam propagation simulation - "Inspection Simulation": Beam interaction with flaws or specimens The user can simulate a whole inspection process (pulse echo, tandem or TOFD) with a wide range of probes (conventional, Phased- arrays or EMAT), components, and flaws.
>

Extended Range Variable Wall® Piping Calibration Blocks for Longseam Inspection

This set of two blocks has been specially designed for situations where ultrasonic examination tak
...
es place circumferentially or “around the curve” for applications such as inspection of longseam welds in piping and vessels. Jointly designed by PH Tool and Holloway NDT, the blocks feature side-drilled hole reflectors positioned within novel compound-curves, each with multiple thickness steps. The unique design results in a light and compact form factor, with the largest block weighing just over 15 lbs and spanning just 16 ¾”. Coverage is provided for nominal pipe sizes from 6” to 10” in the small block and 12” to a whopping 56” in the large block. The compound OD curves and multiple wall thicknesses actually exceed ASME requirements, providing exceptional signal response and measurement accuracy. Properly managing beam divergence off the ID and stabilizing beam skew due to probe rocking is essential to maintaining a consistent calibration when inspecting lengthwise on curved surfaces.
>

ISAFE3 Intrinsically Safe Sensor System

ISAFE3 intrinsically safe sensor system of Vallen Systeme is especially targeted at the petrochemica
...
l - as well as oil and gas transportation industry. The sensor system is designed for permanent monitoring or periodic inspection tasks. Sensors are available for different AE-frequency ranges optimized for corrosion and fatigue crack detection and other applications. The ISAFE 3 sensor system consists of an AE-sensor (model ISAS3) certified according to ATEX/IEC for installation in zone 0, gas group IIC, IP68, 20 to +60 °C, and a signal isolator (model SISO3) certified for installation in zone 2. An ISAS3 sensor can be mounted in atmosphere or submerged, e.g. in water or crude oil. It is supported by mounting tools for temporary (magnets) or permanent (welded) installation. ISAFE3 supports automatic sensor coupling test and can be used with any AE signal processor supporting 28V supply at 90 mA peak, e.g. Vallen Systeme ASIP-2/A.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window