Dissimilar Welds

On 460 welds, between SA213T99 and SA213T22(tubes with 0.5x5mm) has been made a magnetic particle testing.
They were detected 50% of welds with longitudinal linear indications on side TA213T91.
After retesting, by Penetrant testing, only 10% of them have shown indications from cracks.
Why?



 
 Reply 
 
Michael Trinidad
Consultant,
LMATS Pty Ltd , Australia, Joined Jan 2003, 138

Michael Trinidad

Consultant,
LMATS Pty Ltd ,
Australia,
Joined Jan 2003
138
03:46 Nov-24-1999
Re: Dissimilar Welds
This would most likely be the indications from the magnetic leakage field occuring around the large change in permeability between the two disimilar metals. It has often caught out technicians, we had a similar case in the fourm only a few months back.

Kindest Regards

Michael Trinidad


 
 Reply 
 
D. Scott Sullivan
D. Scott Sullivan
01:57 Nov-24-1999
Re: Dissimilar Welds

: This would most likely be the indications from the magnetic leakage field occuring around the large change in permeability between the two disimilar metals. It has often caught out technicians, we had a similar case in the fourm only a few months back.

: Kindest Regards

: Michael Trinidad

: Mr. Trinidad's opinion is most likely correct. Another possibility could be that you were picking up indications of sub-surface lack of fusion with the magnetic particle method. If the lack of fusion was subsurface, the penetrant method would not detect it.
If you cut a cross section and etch the weld, you could confirm this. If you can not cut the weld, a X-ray of the suspect area should be able to readily detect lack of fusion.

:D. Scott Sullivan
Sr. NDT Engineer
RT, ET, MT & PT Level III


 
 Reply 
 
Ken Head
Ken Head
07:56 Nov-24-1999
Re: Dissimilar Welds
:
: : This would most likely be the indications from the magnetic leakage field occuring around the large change in permeability between the two disimilar metals. It has often caught out technicians, we had a similar case in the fourm only a few months back.

: : Kindest Regards

: : Michael Trinidad

: : Mr. Trinidad's opinion is most likely correct. Another possibility could be that you were picking up indications of sub-surface lack of fusion with the magnetic particle method. If the lack of fusion was subsurface, the penetrant method would not detect it.
: If you cut a cross section and etch the weld, you could confirm this. If you can not cut the weld, a X-ray of the suspect area should be able to readily detect lack of fusion.

I think you are mistaken on using X-Ray to determine the presence (or
lack there of) of fusion. As a rule, radiography is not the perferred
method for detecting "non-fusion". the method most suited for this task
is UT.
Ken Head
Sr. Level III
: :D. Scott Sullivan
: Sr. NDT Engineer
: RT, ET, MT & PT Level III




 
 Reply 
 
D. Scott Sullivan
D. Scott Sullivan
06:03 Nov-29-1999
Re: Dissimilar Welds
Ken,

I don't believe I am mistaken regarding the detection of sidewall lack-of-fussion (LOF).

X-ray would be the preffered method. Although you can detect LOF with the ultrasonic method, LOF, weld root cracks and lack-of-penetration (LOP) all give essentially the same type of ultrasonic signal. The reflected signals are narrow and appear at the same location. These signals can in some cases be differentiated by determining the extent of the flaw in the transverse direction. This is not always possible.

In any case, as far as a back-up inspection to MT, I agree that RT or UT could quickly confirm wether or not the MT indication was relevant.

Best Regards,

D. Scott Sullivan



 
 Reply 
 

Product Spotlight

NEW Wheel Type Phased Array Probe

DOPPLER NEW Wheel Type Phased Array Probe, more stable, new tyre makes lesser acoustic attenuation
...
, much lighter makes easier to handle, more slim size, magnetic and mechanical encoder optional etc...more
>

GEKKO - Portable Phased Array Testing with TFM in Real-Time

The portable phased array testing system GEKKO provides 64 parallel test channels. On creating testi
...
ng parameters the operator is assisted by the CIVA software. Due to its modular set-up the GEKKO instrument is suitable for operators of all skill levels.
>

NovaScope 6000

The all-digital Novascope 6000 is a portable, ultra-high precision thickness gauge for high-speed
...
thickness measurement. Novascope 6000 has unmatched capabilities and unique features including: •Superior Resolution with high contrast, high-speed color RF display •High pulser voltage •Real-time video output •Increased internal/external data storage •Programmable SetUp features •Battery & AC Powered
>

Aerospace Systems - Automated Ultrasonic Inspection

USL are specialists in the design and manufacture of turnkey ultrasonic inspection systems for aer
...
ospace applications. From monolithic composites to complex honeycomb structures. This video shows just a few examples of what is possible, find out more at: www.ultrasonic-sciences.co.uk
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window