where expertise comes together - since 1996 -

The Largest Open Access Portal of Nondestructive Testing (NDT)

Conference Proceedings, Articles, News, Exhibition, Forum, Network and more

where expertise comes together
- since 1996 -

Airstar Inc.
Application of the newest technologies, such as air-coupled ultrasound, digital instrumentation, signal processing, and transducer technology.
2138 views
Technical Discussions
Tony Li
Tony Li
09:10 Dec-10-2007
U/T Equipment for Steel Forged Bar

Can anyone advise on suitable U/T equipments for general testing of steel forged round bars (just normal carbon & alloy grades, not for power generation/aerospace usage etc)

We contacted GE and they suggested USM 35X with Dual Element Transducer. Price is very expensive and we really doubt if this is necessary to have this level of equipment.

Also for the transducer, is Single Element Transducer good enough for our product ?

Thanks

Tony Li




 
 Reply 
 
S.V.Swamy
Engineering, - Material Testing Inspection & Quality Control
Retired from Nuclear Fuel Complex , India, Joined Feb 2001, 787

S.V.Swamy

Engineering, - Material Testing Inspection & Quality Control
Retired from Nuclear Fuel Complex ,
India,
Joined Feb 2001
787
04:16 Dec-10-2007
Re: U/T Equipment for Steel Forged Bar
I think you will need a standard ultrasonic flaw detector. Whether you need to use a single element transducer or a dual element transducer, depends on the diameter of the steel bar. Dual element transducers will be needed for smaller diameter bars.

There are many Indian manufacturers of UT flaw detectors and I am sure you can find a good solution with in your budget. I am not connected with any of them and hence I would not recommend specific manufacturers and models etc. I can help you in evaluating the offers which you get, if you need such help.

Swamy
Hyderabad, India


----------- Start Original Message -----------
: Can anyone advise on suitable U/T equipments for general testing of steel forged round bars (just normal carbon & alloy grades, not for power generation/aerospace usage etc)
: We contacted GE and they suggested USM 35X with Dual Element Transducer. Price is very expensive and we really doubt if this is necessary to have this level of equipment.
: Also for the transducer, is Single Element Transducer good enough for our product ?
: Thanks
: Tony Li
------------ End Original Message ------------




 
 Reply 
 
Dent
Consultant, NDE Manager NDELevel III/3
NDT Consultant, Canada, Joined Nov 1998, 248

Dent

Consultant, NDE Manager NDELevel III/3
NDT Consultant,
Canada,
Joined Nov 1998
248
04:38 Dec-10-2007
Re: U/T Equipment for Steel Forged Bar
I test forged bars all day long.
What sizes are your forged bars? This will determine if you need dual elements and what size single elements you need. A basic UT instrument is all you need. There are many inexpensive models out there.

----------- Start Original Message -----------
: I think you will need a standard ultrasonic flaw detector. Whether you need to use a single element transducer or a dual element transducer, depends on the diameter of the steel bar. Dual element transducers will be needed for smaller diameter bars.
: There are many Indian manufacturers of UT flaw detectors and I am sure you can find a good solution with in your budget. I am not connected with any of them and hence I would not recommend specific manufacturers and models etc. I can help you in evaluating the offers which you get, if you need such help.
: Swamy
: Hyderabad, India
:
: : Can anyone advise on suitable U/T equipments for general testing of steel forged round bars (just normal carbon & alloy grades, not for power generation/aerospace usage etc)
: : We contacted GE and they suggested USM 35X with Dual Element Transducer. Price is very expensive and we really doubt if this is necessary to have this level of equipment.
: : Also for the transducer, is Single Element Transducer good enough for our product ?
: : Thanks
: : Tony Li
------------ End Original Message ------------




 
 Reply 
 
chris s
chris s
07:13 Dec-10-2007
Re: U/T Equipment for Steel Forged Bar
----------- Start Original Message -----------
: Can anyone advise on suitable U/T equipments for general testing of steel forged round bars (just normal carbon & alloy grades, not for power generation/aerospace usage etc)
: We contacted GE and they suggested USM 35X with Dual Element Transducer. Price is very expensive and we really doubt if this is necessary to have this level of equipment.
: Also for the transducer, is Single Element Transducer good enough for our product ?
: Thanks
: Tony Li
------------ End Original Message ------------

this inspection can be performed with a relatively cheap analog ut machine ($500), you can look on ebay. your transducer will be Dependant on the bar. i don't think you will need a dual element, a single should work. they are typically more durable anyway


 
 Reply 
 
Tony Li
Tony Li
03:56 Dec-11-2007
Re: U/T Equipment for Steel Forged Bar
----------- Start Original Message -----------
: I think you will need a standard ultrasonic flaw detector. Whether you need to use a single element transducer or a dual element transducer, depends on the diameter of the steel bar. Dual element transducers will be needed for smaller diameter bars.
: There are many Indian manufacturers of UT flaw detectors and I am sure you can find a good solution with in your budget. I am not connected with any of them and hence I would not recommend specific manufacturers and models etc. I can help you in evaluating the offers which you get, if you need such help.
: Swamy
: Hyderabad, India
:
: : Can anyone advise on suitable U/T equipments for general testing of steel forged round bars (just normal carbon & alloy grades, not for power generation/aerospace usage etc)
: : We contacted GE and they suggested USM 35X with Dual Element Transducer. Price is very expensive and we really doubt if this is necessary to have this level of equipment.
: : Also for the transducer, is Single Element Transducer good enough for our product ?
: : Thanks
: : Tony Li
------------ End Original Message ------------

The sizes of our bars are from 250mm to 760mm dia.

And we need to test around 2500mt a month, or 300-400 bars.

U/T standards are mainly ASTM A388, API 6A PSL3, SEP1921 D/c or C/c

I already had several quotes from GE, Sonatest, Newsonic etc. all digital, easy to carry.

Thanks

Tony Li


 
 Reply 
 
S.V.Swamy
Engineering, - Material Testing Inspection & Quality Control
Retired from Nuclear Fuel Complex , India, Joined Feb 2001, 787

S.V.Swamy

Engineering, - Material Testing Inspection & Quality Control
Retired from Nuclear Fuel Complex ,
India,
Joined Feb 2001
787
07:03 Dec-13-2007
Re: U/T Equipment for Steel Forged Bar
----------- Start Original Message -----------
: : I think you will need a standard ultrasonic flaw detector. Whether you need to use a single element transducer or a dual element transducer, depends on the diameter of the steel bar. Dual element transducers will be needed for smaller diameter bars.
: : There are many Indian manufacturers of UT flaw detectors and I am sure you can find a good solution with in your budget. I am not connected with any of them and hence I would not recommend specific manufacturers and models etc. I can help you in evaluating the offers which you get, if you need such help.
: : Swamy
: : Hyderabad, India
: :
: : : Can anyone advise on suitable U/T equipments for general testing of steel forged round bars (just normal carbon & alloy grades, not for power generation/aerospace usage etc)
: : : We contacted GE and they suggested USM 35X with Dual Element Transducer. Price is very expensive and we really doubt if this is necessary to have this level of equipment.
: : : Also for the transducer, is Single Element Transducer good enough for our product ?
: : : Thanks
: : : Tony Li
: The sizes of our bars are from 250mm to 760mm dia.
: And we need to test around 2500mt a month, or 300-400 bars.
: U/T standards are mainly ASTM A388, API 6A PSL3, SEP1921 D/c or C/c
: I already had several quotes from GE, Sonatest, Newsonic etc. all digital, easy to carry.
: Thanks
: Tony Li
------------ End Original Message ------------

300 - 400 bars a month translates to about 15 bars a day and can be done manually. The selection of the probe depends on the defect to be detected. Check out the model with the best price.

Swamy



 
 Reply 
 

Product Spotlight

Semi-Automated Phased Array Immersion System for Small Composite Parts

Turn-key semi-automated system as an improved and affordable solution for inspection of small comp
...
osite parts. Includes support table, immersion tank, scanner, PA instrument, PC, Analysis software, database, wedge management and other options.
>

Magnetic X-Ray Pipeline Crawler

Zhong Yi brand pipeline crawler is magnetic/micro-video controlled crawler with DC X ray unit inst
...
alled for checking welding of pipeline. Move steadily inside the pipeline 6''-60''diameter with speed of up to 18m/min, Max. moving diatance 5 kilometers and provide the efficient inspection of the pipeline.
>

Panther

M2M PANTHER is a phased-array equipment designed for both desktop and industrial applications, offer
...
ing unparalleled performance in a compact unit. It combines the speed required for industrial integrated Phased-Array Ultrasound (PAUT) solutions, with the most complete set of total focusing method (TFM) imaging techniques, making it the ultimate tool for R&D and procedure qualification.
>

iProbe - USB Phased Array Probe

Turn your PC, Laptop or Tablet into a powerful 32:64 Phased Array system with our USB powered Phas
...
ed Array iProbe and inspection software package. Perform affordable weld inspection and corrosion mapping inspections with this powerful but small system. The probe has a 100V pulser, 8K PRF, dual axis encoder input and achieves outstanding signal quality.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window