Technical Discussions
Kumar
Kumar
03:48 Aug-25-2008
ASME Code Case 2235 Qualification blocks

Could anyone tell me where can I have the UT qualification/demonstration blocks made to ASME Code case 2235? The flaws are supposed to be actual flaws generated by welding.

Thks!


    
 
 Reply 
 
mj
mj
00:08 Aug-26-2008
Re: ASME Code Case 2235 Qualification blocks
Dear Friend, as per code case 2235-09 qualification block shall be prepared by welding or HIP and ahll contain 3 flaws( it maybe a diffect or notch/side drilled hole. the diffrence between both calibration and qualification block is, one made just in a plate and other in a welding, also usualy if u make a small thickness qualificatin block during welding u can keep some welding rod inside and weld. also you can keep a RT report for the block. iam sure flaw maybe a natural defect or artificial!!!! always iam making this kind of blocks
Please let me know others comment. if iam not right please respond.

mj


----------- Start Original Message -----------
: Could anyone tell me where can I have the UT qualification/demonstration blocks made to ASME Code case 2235? The flaws are supposed to be actual flaws generated by welding.
: Thks!
------------ End Original Message ------------




    
 
 Reply 
 
mustafa GONULAL
Engineering,
CIMTAS / ENKA, Turkey, Joined Jun 2008, 8

mustafa GONULAL

Engineering,
CIMTAS / ENKA,
Turkey,
Joined Jun 2008
8
00:49 Aug-27-2008
Re: ASME Code Case 2235 Qualification blocks
Dear peers,
I am drawing and producing calibration and qualification blocks over 4 years. If you want to know more detail contact with me via e-mail.

----------- Start Original Message -----------
: Dear Friend, as per code case 2235-09 qualification block shall be prepared by welding or HIP and ahll contain 3 flaws( it maybe a diffect or notch/side drilled hole. the diffrence between both calibration and qualification block is, one made just in a plate and other in a welding, also usualy if u make a small thickness qualificatin block during welding u can keep some welding rod inside and weld. also you can keep a RT report for the block. iam sure flaw maybe a natural defect or artificial!!!! always iam making this kind of blocks
: Please let me know others comment. if iam not right please respond.
: mj
:
: : Could anyone tell me where can I have the UT qualification/demonstration blocks made to ASME Code case 2235? The flaws are supposed to be actual flaws generated by welding.
: : Thks!
------------ End Original Message ------------




    
 
 Reply 
 
Michael Moles †2014 *1948
, Joined ,
02:44 Aug-28-2008
Re: ASME Code Case 2235 Qualification blocks
----------- Start Original Message -----------
: Dear peers,
: I am drawing and producing calibration and qualification blocks over 4 years. If you want to know more detail contact with me via e-mail.
: : Dear Friend, as per code case 2235-09 qualification block shall be prepared by welding or HIP and ahll contain 3 flaws( it maybe a diffect or notch/side drilled hole. the diffrence between both calibration and qualification block is, one made just in a plate and other in a welding, also usualy if u make a small thickness qualificatin block during welding u can keep some welding rod inside and weld. also you can keep a RT report for the block. iam sure flaw maybe a natural defect or artificial!!!! always iam making this kind of blocks
: : Please let me know others comment. if iam not right please respond.
: : mj
: :
: : : Could anyone tell me where can I have the UT qualification/demonstration blocks made to ASME Code case 2235? The flaws are supposed to be actual flaws generated by welding.
: : : Thks!
------------ End Original Message ------------

Unfortunately, you are not correct in your interpretation. While the original ASME CC 2235 was not clear on this issue, the intent was to use artificial cracks - not side drilled holes or notches - as the reflectors. In addition, the artificial cracks should follow the bevel to simulate Lack of Fusion defects or similar. ASME is currently working on clarifying this situation.

Michael Moles
Member, ASME Section V Ultrasonics Working Group



    
 
 Reply 
 
mj
mj
09:04 Aug-30-2008
Re: ASME Code Case 2235 Qualification blocks
----------- Start Original Message -----------
: : Dear peers,
: : I am drawing and producing calibration and qualification blocks over 4 years. If you want to know more detail contact with me via e-mail.
: : : Dear Friend, as per code case 2235-09 qualification block shall be prepared by welding or HIP and ahll contain 3 flaws( it maybe a diffect or notch/side drilled hole. the diffrence between both calibration and qualification block is, one made just in a plate and other in a welding, also usualy if u make a small thickness qualificatin block during welding u can keep some welding rod inside and weld. also you can keep a RT report for the block. iam sure flaw maybe a natural defect or artificial!!!! always iam making this kind of blocks
: : : Please let me know others comment. if iam not right please respond.
: : : mj
: : :
: : : : Could anyone tell me where can I have the UT qualification/demonstration blocks made to ASME Code case 2235? The flaws are supposed to be actual flaws generated by welding.
: : : : Thks!
: Unfortunately, you are not correct in your interpretation. While the original ASME CC 2235 was not clear on this issue, the intent was to use artificial cracks - not side drilled holes or notches - as the reflectors. In addition, the artificial cracks should follow the bevel to simulate Lack of Fusion defects or similar. ASME is currently working on clarifying this situation.
: Michael Moles
: Member, ASME Section V Ultrasonics Working Group
------------ End Original Message ------------

Thanks Michael we are only using code case 2235-09 or asme sec.V for the inspection . sure i did atleast 25 project using the same code and with a normal demo block. if something diffrent come out from ASME we will follow it
MJ


    
 
 Reply 
 
EC
EC
00:09 Sep-10-2008
Re: ASME Code Case 2235 Qualification blocks
----------- Start Original Message -----------
: : : Dear peers,
: : : I am drawing and producing calibration and qualification blocks over 4 years. If you want to know more detail contact with me via e-mail.
: : : : Dear Friend, as per code case 2235-09 qualification block shall be prepared by welding or HIP and ahll contain 3 flaws( it maybe a diffect or notch/side drilled hole. the diffrence between both calibration and qualification block is, one made just in a plate and other in a welding, also usualy if u make a small thickness qualificatin block during welding u can keep some welding rod inside and weld. also you can keep a RT report for the block. iam sure flaw maybe a natural defect or artificial!!!! always iam making this kind of blocks
: : : : Please let me know others comment. if iam not right please respond.
: : : : mj
: : : :
: : : : : Could anyone tell me where can I have the UT qualification/demonstration blocks made to ASME Code case 2235? The flaws are supposed to be actual flaws generated by welding.
: : : : : Thks!
: : Unfortunately, you are not correct in your interpretation. While the original ASME CC 2235 was not clear on this issue, the intent was to use artificial cracks - not side drilled holes or notches - as the reflectors. In addition, the artificial cracks should follow the bevel to simulate Lack of Fusion defects or similar. ASME is currently working on clarifying this situation.
: : Michael Moles
: : Member, ASME Section V Ultrasonics Working Group
: Thanks Michael we are only using code case 2235-09 or asme sec.V for the inspection . sure i did atleast 25 project using the same code and with a normal demo block. if something diffrent come out from ASME we will follow it
: MJ
------------ End Original Message ------------

Hello, we are working with TOFD inspection procedures following ASME V and VIII and we've a problem with the interpretation of the qualification block's thickness. Could somebody explain us what thickness we must choose for a range of inspection of 25 to 200 mm?
thanks!!!!


    
 
 Reply 
 
Nigel Armstrong
Engineering, - Specialist services
United Kingdom, Joined Oct 2000, 1096

Nigel Armstrong

Engineering, - Specialist services
United Kingdom,
Joined Oct 2000
1096
01:17 Sep-10-2008
Re: ASME Code Case 2235 Qualification blocks
Hi EC

You should read the 2007 Edition of ASME V, Article 4 Mandatory Appendix III, TOFD of welds. Calibration block thickness and range qualified are clearly stated in III-434.

Regards

Nigel

----------- Start Original Message -----------
: : : : Dear peers,
: : : : I am drawing and producing calibration and qualification blocks over 4 years. If you want to know more detail contact with me via e-mail.
: : : : : Dear Friend, as per code case 2235-09 qualification block shall be prepared by welding or HIP and ahll contain 3 flaws( it maybe a diffect or notch/side drilled hole. the diffrence between both calibration and qualification block is, one made just in a plate and other in a welding, also usualy if u make a small thickness qualificatin block during welding u can keep some welding rod inside and weld. also you can keep a RT report for the block. iam sure flaw maybe a natural defect or artificial!!!! always iam making this kind of blocks
: : : : : Please let me know others comment. if iam not right please respond.
: : : : : mj
: : : : :
: : : : : : Could anyone tell me where can I have the UT qualification/demonstration blocks made to ASME Code case 2235? The flaws are supposed to be actual flaws generated by welding.
: : : : : : Thks!
: : : Unfortunately, you are not correct in your interpretation. While the original ASME CC 2235 was not clear on this issue, the intent was to use artificial cracks - not side drilled holes or notches - as the reflectors. In addition, the artificial cracks should follow the bevel to simulate Lack of Fusion defects or similar. ASME is currently working on clarifying this situation.
: : : Michael Moles
: : : Member, ASME Section V Ultrasonics Working Group
: : Thanks Michael we are only using code case 2235-09 or asme sec.V for the inspection . sure i did atleast 25 project using the same code and with a normal demo block. if something diffrent come out from ASME we will follow it
: : MJ
: Hello, we are working with TOFD inspection procedures following ASME V and VIII and we've a problem with the interpretation of the qualification block's thickness. Could somebody explain us what thickness we must choose for a range of inspection of 25 to 200 mm?
: thanks!!!!
------------ End Original Message ------------




    
 
 Reply 
 
David Mackintosh
Engineering,
Acuren Group Inc., Canada, Joined Feb 2011, 85

David Mackintosh

Engineering,
Acuren Group Inc.,
Canada,
Joined Feb 2011
85
08:54 Dec-12-2008
Re: ASME Code Case 2235 Qualification blocks
----------- Start Original Message -----------
: Hi EC
: You should read the 2007 Edition of ASME V, Article 4 Mandatory Appendix III, TOFD of welds. Calibration block thickness and range qualified are clearly stated in III-434.
: Regards
: Nigel
-------------------------------------------------

I believe that Appendix III only specifies the CALIBRATION block. For the QUALIFICATION block, Code Case 2235 only requires the three flaws and says very little about the block design. It is up to the Owner to design a qualification/demonstration block specific to their needs.

David


    
 
 Reply 
 

Product Spotlight

FAAST-PA! OEM Patented phased Array for high speed UT inspection

Multiangle, Multifocus, Multifrequency, Multibeam. Instead of stacking UT electronics and having m
...
any PA probes, FAAST-PA is able to transmit all delay laws within ONE single shot in Real time.
>

Combination of Digital Image Correlation and Thermographic Measurements

The combination of measuring results from the digital image correlation (ARAMIS, DIC) and temperat
...
ure measuring data from infrared cameras permits the simultaneous analysis of the thermal and mechanical behavior of test specimens in the materials and components testing field.
>

Immersion systems

ScanMaster ultrasonic immersion systems are designed for high throughput, multi shift operation in a
...
n industrial or lab environment. These fully integrated systems provide various scanning configurations and incorporate conventional and phased arrays technologies to support diverse applications, such as inspection of disks, bars, shafts, billets and plates. All of ScanMaster immersion systems are built from high accuracy scanning frames allowing for scanning of complex parts and include a multi-channel ultrasonic instrument with exceptional performance. The systems are approved by all major manufacturers for C-scan inspection of jet engine forged discs. Together with a comprehensive set of software modules these flexible series of systems provide the customer with the best price performance solutions.
>

NDT Master Lecturer

In the program both university professors and practitioners will give lectures, which guarantees the
...
oretical depth and practical inside. Academic Director: Prof. Dr. Christian Boller
The following lecturers are not complete: Prof. Tadeusz Stepinski, Prof. Wieslaw Staszewski, Prof. Frank Walther, Prof. Giovanni Bruno, Prof. Gerd Dobmann, Prof. Philippe Guy
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window