Technical Discussions
Brian Younce
Brian Younce
05:13 Dec-20-2000
Mechanical Cleaning Prior To Magnetic Particle Inspection

NDT Folks,
I am wondering if anyone has information regarding mechanical cleaning prior to magnetic particle inspection. The specific application would be removing heat treat scale prior to magnetic particle inspection. One method that we are considering is a glass media blast. My concerns would be metal smearing or discontinuity contamination.
I would like to hear of any specific practices which some of you may use for this same type of application. Thank you in advance for any help.
Regards,
Brian


 
 Reply 
 
Dave Ronson
Dave Ronson
06:16 Dec-20-2000
Re: Mechanical Cleaning Prior To Magnetic Particle Inspection
: NDT Folks,
: I am wondering if anyone has information regarding mechanical cleaning prior to magnetic particle inspection. The specific application would be removing heat treat scale prior to magnetic particle inspection. One method that we are considering is a glass media blast. My concerns would be metal smearing or discontinuity contamination.
: I would like to hear of any specific practices which some of you may use for this same type of application. Thank you in advance for any help.
: Regards,
: Brian

I would suggest you try using a chemical such as Ardrox 185 used with Ardrox 188 a high alkaline type product which is made for steel components to remove heat scale. Unfortnatlry, you will have to heat both products to around 180 degrees F. It is not a feild application.




 
 Reply 
 
Tom Murphy
NDT Inspector
USA, Joined Jul 2000, 16

Tom Murphy

NDT Inspector
USA,
Joined Jul 2000
16
06:39 Dec-20-2000
Re: Mechanical Cleaning Prior To Magnetic Particle Inspection
We commonly use glass bead blasting. We perform MT
inspection of steam turbine components after a period
of service. They have heat scale after they have run
for awhile. Our procedure requires that the glass
shot should be of a high grade crown glass of the
soda lime type with silica content >62%. It also
recommends a spherical shape and bead diameters of
0.006 inches to 0.010 inches in diameter. The beads
are not to be reused.

Regards,
Tom

: NDT Folks,
: I am wondering if anyone has information regarding mechanical cleaning prior to magnetic particle inspection. The specific application would be removing heat treat scale prior to magnetic particle inspection. One method that we are considering is a glass media blast. My concerns would be metal smearing or discontinuity contamination.
: I would like to hear of any specific practices which some of you may use for this same type of application. Thank you in advance for any help.
: Regards,
: Brian




 
 Reply 
 
Barry J Gordon
Barry J Gordon
01:50 Dec-20-2000
Re: Mechanical Cleaning Prior To Magnetic Particle Inspection
: NDT Folks,
: I am wondering if anyone has information regarding mechanical cleaning prior to magnetic particle inspection. The specific application would be removing heat treat scale prior to magnetic particle inspection. One method that we are considering is a glass media blast. My concerns would be metal smearing or discontinuity contamination.
: I would like to hear of any specific practices which some of you may use for this same type of application. Thank you in advance for any help.
: Regards,
: Brian


Brian,

In circumstances where we don't want discontinuity contamination such as turbine blades we use bicarb soda blasting. It is very gentle on the parent material but will still remove a strong build up of scale and has the added advantage of being environmentally friendly.


 
 Reply 
 

Product Spotlight

On-Demand Webinar: Advanced Ultrasonic Techniques for HTHA Detection & Assessment

In the Oil and Gas industry, High Temperature Hydrogen Attack (HTHA) can occur in steels operating a
...
t high temperature, usually above 205°C (400°F). Early stages of HTHA are very difficult to detect. Join us for a webinar presented by Guy Maes, Zetec Sales Engineer Director. The webinar will demonstrate how advanced ultrasonic techniques are deployed for efficient and reliable HTHA inspections.
>

HARDNESS TESTER TKM-459CE combi

TKM-459CE combi applies 2 methods of hardness control: UCI and Leeb. It provides high-accuracy tes
...
ting of metals and alloys as well as items of different sizes and configurations, their hardened layers and galvanic coatings. Device represents results in HB, HRC, HV and others. Shock-, dust- and water-proof housing with intuitive software make this gauge easy to use in all working conditions.
>

CIVA 2020 UT Module

CIVA NDE Simulation Software is the world leader of NDT Simulation. The UT simulation Module incl
...
udes: - "Beam computation": Beam propagation simulation - "Inspection Simulation": Beam interaction with flaws or specimens The user can simulate a whole inspection process (pulse echo, tandem or TOFD) with a wide range of probes (conventional, Phased- arrays or EMAT), components, and flaws.
>

NEW Wheel Type Phased Array Probe

DOPPLER NEW Wheel Type Phased Array Probe, more stable, new tyre makes lesser acoustic attenuation
...
, much lighter makes easier to handle, more slim size, magnetic and mechanical encoder optional etc...more
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window