Brian Younce
Brian Younce
05:13 Dec-20-2000
Mechanical Cleaning Prior To Magnetic Particle Inspection

NDT Folks,
I am wondering if anyone has information regarding mechanical cleaning prior to magnetic particle inspection. The specific application would be removing heat treat scale prior to magnetic particle inspection. One method that we are considering is a glass media blast. My concerns would be metal smearing or discontinuity contamination.
I would like to hear of any specific practices which some of you may use for this same type of application. Thank you in advance for any help.
Regards,
Brian


 
 Reply 
 
Dave Ronson
Dave Ronson
06:16 Dec-20-2000
Re: Mechanical Cleaning Prior To Magnetic Particle Inspection
: NDT Folks,
: I am wondering if anyone has information regarding mechanical cleaning prior to magnetic particle inspection. The specific application would be removing heat treat scale prior to magnetic particle inspection. One method that we are considering is a glass media blast. My concerns would be metal smearing or discontinuity contamination.
: I would like to hear of any specific practices which some of you may use for this same type of application. Thank you in advance for any help.
: Regards,
: Brian

I would suggest you try using a chemical such as Ardrox 185 used with Ardrox 188 a high alkaline type product which is made for steel components to remove heat scale. Unfortnatlry, you will have to heat both products to around 180 degrees F. It is not a feild application.




 
 Reply 
 
Tom Murphy
NDT Inspector
USA, Joined Jul 2000, 16

Tom Murphy

NDT Inspector
USA,
Joined Jul 2000
16
06:39 Dec-20-2000
Re: Mechanical Cleaning Prior To Magnetic Particle Inspection
We commonly use glass bead blasting. We perform MT
inspection of steam turbine components after a period
of service. They have heat scale after they have run
for awhile. Our procedure requires that the glass
shot should be of a high grade crown glass of the
soda lime type with silica content >62%. It also
recommends a spherical shape and bead diameters of
0.006 inches to 0.010 inches in diameter. The beads
are not to be reused.

Regards,
Tom

: NDT Folks,
: I am wondering if anyone has information regarding mechanical cleaning prior to magnetic particle inspection. The specific application would be removing heat treat scale prior to magnetic particle inspection. One method that we are considering is a glass media blast. My concerns would be metal smearing or discontinuity contamination.
: I would like to hear of any specific practices which some of you may use for this same type of application. Thank you in advance for any help.
: Regards,
: Brian




 
 Reply 
 
Barry J Gordon
Barry J Gordon
01:50 Dec-20-2000
Re: Mechanical Cleaning Prior To Magnetic Particle Inspection
: NDT Folks,
: I am wondering if anyone has information regarding mechanical cleaning prior to magnetic particle inspection. The specific application would be removing heat treat scale prior to magnetic particle inspection. One method that we are considering is a glass media blast. My concerns would be metal smearing or discontinuity contamination.
: I would like to hear of any specific practices which some of you may use for this same type of application. Thank you in advance for any help.
: Regards,
: Brian


Brian,

In circumstances where we don't want discontinuity contamination such as turbine blades we use bicarb soda blasting. It is very gentle on the parent material but will still remove a strong build up of scale and has the added advantage of being environmentally friendly.


 
 Reply 
 

Product Spotlight

VeeScan AirCraft Wheel Inspection

The VEESCAN offers maximum flexibility, has a proven mechanical design and records of breakdown-fr
...
ee operation of over 365 days. Appealing to companies in the Aerospace industry, the VEESCAN is ideal for all wheel-testing environments. With a wide selection of probes, the VeeScan allows your wheel testing facility the flexibility to select the most compatible configurations with their workload.
>

Eddy Current inspection : RotoETscan Rotating Head

The rotating head RotoETscan detects the presence of longitudinal surface or sub surface defects a
...
t high speed. The rotating head is often installed directly on the production line. It is generally dedicated to the control of long products such as tubes, bars and wires, made of ferrous or non-ferrous material. It can also be used for inspection of small parts (billets).
>

TESTD-PT SYSTEM

Pulse thermography is a non-contact test method that is ideal for the characterization of thin fil
...
ms and coatings or the detection of defects. With a remarquable short test time and a high detection sensitivity, the Telops TESTD-PT is the perfect tool for non- destructive testing. With such high frame rates, it is even possible to investigate highly conductive or diffusive materials.
>

GUL Subsea Solutions - Screeening & Monitoring

To inspect new and existing subsea lines, you need proven technology and experience. GUL offers it's
...
technology to solve this challenge: GUL Subsea and gMAT Transducer Rings.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window