krish
krish
12:07 May-06-2009
Acoustic emission testing of HIC affected pressure vessel

I would like to have the expert opinion about real time monitoring of Hydrogen Induced Cracking in a glass flake lined pressure vessel using Acoustic Emission Testing if condition favours to use the technique. Is it possible to detect step wise cracking & blister growth?

regards,

 
 Reply 
 
bob sudharmin
Engineering, Reliability and Integrity Eng
Shell Malaysia Trading, Malaysia, Joined Jan 2008, 54

bob sudharmin

Engineering, Reliability and Integrity Eng
Shell Malaysia Trading,
Malaysia,
Joined Jan 2008
54
17:08 May-06-2009
Re: Acoustic emission testing of HIC affected pressure vessel
In Reply to krish at 12:07 May-06-2009 (Opening).

Interesting question. I am no expert in this field, but what I understand is that Acoustic Emission listens to corrosion activity and hence translates to possible loss of metal or even leaks.
Its also interesting to know about Hydrogen Induced Cracking which normally happens in a non coated pressure vessel and how this can happen in a glass flake lined vessel.
For step wise cracking & blister growth, Ultrasonics would still be the best detection and monitoring procedure, and surely I would also like to know more of whether AE is also capable of doing this

 
 Reply 
 
Roger Duwe
NDT Inspector, API-510, 570, 653
MISTRAS, USA, Joined Jan 2009, 148

Roger Duwe

NDT Inspector, API-510, 570, 653
MISTRAS,
USA,
Joined Jan 2009
148
23:23 May-06-2009
Re: Acoustic emission testing of HIC affected pressure vessel
In Reply to bob sudharmin at 17:08 May-06-2009 .

I'm a 'user', not a subject expert.

Blister growth = Maybe

Stepwise, or any other crack propagation = Absolutely! This assumes that it is possible to stress the vessel, by pressuring it up to a psi at least 10% about the highest it has seen in the last year or so.

20 or 40% above the last highest pressure used at will give much better results. What you are doing is listening for flaws to propagate under the increased stress. The more [safe] stress, the better, and the smaller defects that can be identified.

 
 Reply 
 
John O'Brien
Consultant, -
Chevron ETC , USA, Joined Jan 2000, 280

John O'Brien

Consultant, -
Chevron ETC ,
USA,
Joined Jan 2000
280
21:31 May-07-2009
Re: Acoustic emission testing of HIC affected pressure vessel
In Reply to Roger Duwe at 23:23 May-06-2009 .

There was a report on work I think published by NACE a number of years ago that looked at the ability of AE to detect activity from HIC. Basically any propogation of the blister towards a step or the step cracks themselves will generate AE. Since then a number of people have monitored vessels with some success. A large amount of the hydrocarbon industry vessel population is made for SA 516 Grade 70 and this is a 'quiet' steel so density and placement of sensors can be crucial. Be aware that permenet moniroing may be more effective for results than 'intervention' testing by raising pressure.

Interetsing that this is an internally lined vessel and you still have HIC. Since you presumably have access to teh external surface I would still wonder why you are not AUT mapping the affected area or is your suspected hydrogen charging rate so high you fear rapid propogation.

 
 Reply 
 
krish
krish
10:13 May-08-2009
Re: Acoustic emission testing of HIC affected pressure vessel
In Reply to John O'Brien at 21:31 May-07-2009 .

Thanks john and other for the expert comments.We did AUT scan and TOFD and found laminar type of indication at the mid wall of the plate close to the L-Seam/C-Seam welds.Originally the vesseal was coated with Coal Tar epoxy and latter it was upgraded with Glass flake vinyl ester.Thro AE we want to ensure whether the existing lamination/dense inclusion at the mid wall is growing or not in service.There is a possibility that it could be pre-existing manufacturing defect and hence it is operating under moderate H2S environment that we feels that the defective site will favor for hic to initiate.

 
 Reply 
 

Product Spotlight

Immersion systems

ScanMaster ultrasonic immersion systems are designed for high throughput, multi shift operation in a
...
n industrial or lab environment. These fully integrated systems provide various scanning configurations and incorporate conventional and phased arrays technologies to support diverse applications, such as inspection of disks, bars, shafts, billets and plates. All of ScanMaster immersion systems are built from high accuracy scanning frames allowing for scanning of complex parts and include a multi-channel ultrasonic instrument with exceptional performance. The systems are approved by all major manufacturers for C-scan inspection of jet engine forged discs. Together with a comprehensive set of software modules these flexible series of systems provide the customer with the best price performance solutions.
>

TESTD-PT SYSTEM

Pulse thermography is a non-contact test method that is ideal for the characterization of thin fil
...
ms and coatings or the detection of defects. With a remarquable short test time and a high detection sensitivity, the Telops TESTD-PT is the perfect tool for non- destructive testing. With such high frame rates, it is even possible to investigate highly conductive or diffusive materials.
>

Robotic laser shearography enables 100% inspection of complex, flight-critical composite structures

An article in “Composites World Magazine” showcases Non Destructive Testing of aero-structures
...
with Laser Shearography. Over the years Dantec Dynamics has supplied many solutions for the aerospace industry. Referring to specific customer projects several of these cases are examined to outline the advantages of using Laser Shearography for automated defect detection.
>

GUL QSR1® Scanning

How do you measure pipe wall thickness without direct access to the area? QSR® Scanning - Guide Wav
...
e Quantitative Short Range Scanning.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window