Mondonico Luca
NDT Inspector
SICES S.p.A., Italy, Joined May 2009, 7

Mondonico Luca

NDT Inspector
SICES S.p.A.,
Italy,
Joined May 2009
7
13:50 Dec-02-2009
Cobalto 60

Do anyone have experience about a gammagrafic exposure with Cobalto 60 on welds having a thickness of 260mm?

 
 Reply 
 
Slawomir Mackiewicz
Slawomir Mackiewicz
20:18 Dec-02-2009
Re: Cobalto 60
In Reply to Mondonico Luca at 13:50 Dec-02-2009 (Opening).

I think it is rather unusual task to do Co-60 exposures on 260 mm (steel) wall thickness. Below I am pointing out some problems with such examination.

1. The European standards EN 444 and EN 1435 covering RT testing of welds limit the use of Co-60 to 200 mm of steel for Class A and to 150 mm of steel for Class B. So you can have a formal problem with the standard compliance.

2. For 260 mm thickness of steel the scattered radiation Build-up Factor for Co-60 emission lines (1,17 and 1,32 MeV) is about 11. It means that the image forming primary radiation stands for less than 10% of the total radiation reaching the film. You surely obtain very poor IQI sensitivity.

3. To meet the EN 1435 requirements for geometric unsharpness for 260 mm wall thickness and typical 5 mm source size you should use SFD not less than 3315 mm.

4. For such SFD, even using 100 Ci source and D7 film you get exposure times of the order of 1000 hours !!!. Even if you break the rules and use SFD=1000 mm you get unacceptable exposure times of the order of 100 hours.

So my advice is: forget about Cobalt radiography for 260 mm thick steel and think about TOFD or other UT technique.

 
 Reply 
 
Mondonico Luca
NDT Inspector
SICES S.p.A., Italy, Joined May 2009, 7

Mondonico Luca

NDT Inspector
SICES S.p.A.,
Italy,
Joined May 2009
7
11:29 Dec-03-2009
Re: Cobalto 60
In Reply to Slawomir Mackiewicz at 20:18 Dec-02-2009 .

I'm completely agree with you, but the final user doesn't accept TOFD examination.
I'm making some test in the bunker, but i'm not sure to obtain a satisfactory result.
Canyou explan better tour point 2?
How are you able to say that the scattered radiation Bulid-up Factor is about 11 and the image forming primary radiation stands for less than 10% of the total radiation reaching the film?
Thank you

 
 Reply 
 
anjafo79
NDT Inspector
Norway, Joined Aug 2009, 204

anjafo79

NDT Inspector
Norway,
Joined Aug 2009
204
12:32 Dec-03-2009
Re: Cobalto 60
In Reply to Mondonico Luca at 11:29 Dec-03-2009 .

Doubt you will find many welding defects this way unless they are huge :)

You can suggest to do x-ray at different weld stages such as after first run, 1/3 and 1/2 welded butt. This way you have some record of the welded joint and complement this with Ultrasonic, MPI/DPI and Visual (even at the same stages?).

 
 Reply 
 
Slawomir Mackiewicz
Slawomir Mackiewicz
19:59 Dec-03-2009
Re: Cobalto 60
In Reply to Mondonico Luca at 11:29 Dec-03-2009 .

Luca

The radiation Build-up Factor, B is not a kind of thing easy to explain in a few words. In short, it is a number by which you have to multiply the intensity of primary radiation (i.e. radiation not scattered within the material) passing the certain material thickness to obtain the TOTAL intensity of radiation passing through this thickness. This TOTAL is the sum of primary and scattered radiation.

So if, the build up factor for your 260 mm steel slab is B=11 it means that the total radiation intensity registered behind your slab is 11 times greater than the intensity of its primary component. In other words “good”, image building, primary radiation stands only for 1/11 (9,1%) of the total radiation registered by your film.

The comprehensive tables of build-up factors for different materials and radiation energies you can find in ANSI/ANS-6.4.3.

Theory is a theory but you mentioned that you have made some practical trials with Cobalt exposures of 260 mm thick steel. I am really curies to your results. What exposure parameters did you use and what film densities and IQI sensitivities did you really obtain.

Best Regards
Slawomir

 
 Reply 
 
Nigel Armstrong
Engineering, - Specialist services
United Kingdom, Joined Oct 2000, 1096

Nigel Armstrong

Engineering, - Specialist services
United Kingdom,
Joined Oct 2000
1096
12:57 Dec-04-2009
Re: Cobalto 60
In Reply to Mondonico Luca at 11:29 Dec-03-2009 .

I'm sorry Mondonico but i have to ask this - have you asked your end-user to state why they insist on Gamma ray under such unusual and dangerous conditions - especially relevant to the excellent considerations put forward by Slawomir? And have they given a clear and unequivocal answer? Or conceded the need, as per Anjafo's post, for intermediate and supplementary inspections? It should be relatively easy for you to provide evidence after a literature search that the TOFD method has a higher probability of detection (POD) than Cobalt gamma ray for heavy wall weld examination. And if you are going ahead with a formal reported inspection make certain you record your doubts in a formal and traceable manner. A signed accepting report with no inadequacy statement is of no benefit to you in case of any manufacturing history investigation - after all 260mm thick steel has a special application.

Perhaps there are conditions such as the acceptance criteria or expected defect types which mitigate for Cobalt gamma, but I would be wondering about the hidden agenda of your end-user. Clue: are they the real end-user or are they the EPMC?

 
 Reply 
 
Roger Duwe
NDT Inspector, API-510, 570, 653
MISTRAS, USA, Joined Jan 2009, 148

Roger Duwe

NDT Inspector, API-510, 570, 653
MISTRAS,
USA,
Joined Jan 2009
148
18:16 Dec-07-2009
Re: Cobalto 60
In Reply to Nigel Armstrong at 12:57 Dec-04-2009 .

I concurr with Mr. Armstrong. TOFD will find all significant defects. Cobalt 60 at that thickness will only find HUGE defects, and that lack of sensitivity will be shown by your penetrameter / Image Quality Indicator. The people you are talking to may not want you to find moderate sized defects.

Any reputable engineer would not demand that you perform NDT outside of the ASME and EN limits. Those limits were established based on experience, and proven [and disproven] capabilities. You are trying to go beyond a physical limitation, as evidenced by Mr. Mackiewicz's calculations.

I strongly recommend that you stay within ASME and/or EN limits. Knowingly going outside established Codes and Standards opens your company up to masssive liability.

 
 Reply 
 

Product Spotlight

EKOSCAN Phased Array

In order to always fit your needs, EKOSCAN can manufacture any type of UT transducer, either convent
...
ional or Phased Array. As an ISO 9001: 2015 certified company, EKOSCAN is extremely careful as far a material selection and manufacturing processes are concerned. Our probes guarantee our customers the benefits of latest innovations regarding piezo-composite, backing, impedance adaptation layer, etc. Specific probes for hostile environment: high temperature, high pressure, corrosive environment,etc. Specific probes designed to fit your specific application: optimization of every parameter to guarantee you the best detection.
>

MUSE Mobile Ultrasonic Equipment

The MUSE, a portable ultrasonic imaging system, was developed for in-field inspections of light-weig
...
ht structures. The MUSE consists of a motor-driven manipulator, a water circulation system for the acoustic coupling and a portable ultrasonic flaw detector (USPC 3010). The MUSE provides images of internal defects (A-, B-,C- and D-scan).
>

Research Center IDEKO develops an ultrasonic train wheel inspection system for CAF

The Basque Research centre IK4-IDEKO has developed a state-of-the-art ultrasonic inspection system f
...
or the train wheel. This system secures a sound condition of train wheels and is thus a significant contribution to rail transport safety. The device was delivered to CAF recently and its use allows the manufacturer to become an approved supplier of rolling stock in Italy, as it meets the demanding homologation standards of this country. \\\\r\\\\n
>

Navic - Steerable Modular Automated Scanner

The Navic is a modular, motorized, steerable scanner designed to carry multiple attachments used
...
in various scanning and inspection applications. The Navic is capable of weld scanning (girth welds and long seam welds), automated corrosion mapping, and tank scanning.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window