Technical Discussions
Brian Younce
Brian Younce
00:55 Oct-09-2002
Pre-penetrant Surface Prep of an EDM Cut Aluminum Surface

Folks,

I am wondering if anyone can reference me to information regarding surface preparation of an EDM cut aluminum surface that is to be penetrant inspected. My concerns are whether etching should be required or not, if so how aggressive of an etch, if not is there a different surface prep that is recommended. Does the EDM process have the tendency to smear metal, close pre-existing discontinuities, create new discontinuities?

I am not familiar with the EDM process, therefore I have more questions than answers at this point and would appreciate any input from anyone who does have some experience.

Thanks in advance for your time,

Brian Younce
NDT Level III
Hartzell Propeller Inc.



    
 
 Reply 
 
Phil Herman Jr.
Sales, - Manufacture of NDT Reference Standards/Test Blocks
PH Tool Reference Standards, USA, Joined Oct 1999, 79

Phil Herman Jr.

Sales, - Manufacture of NDT Reference Standards/Test Blocks
PH Tool Reference Standards,
USA,
Joined Oct 1999
79
01:15 Oct-09-2002
Re: Pre-penetrant Surface Prep of an EDM Cut Aluminum Surface
Brian,

PH Tool Reference Standards manufactures EDM notch standards and test blocks for all NDT disciplines. While we are most familiar with the "micro-machining" of narrow notches and slots, we also perform both conventional (a.k.a. sinker) and wire EDM. It would be helpful to know which process was used to manufacture the aluminum parts you need to PT. Feel free to contact me directly at 888-553-9245 or philjr@phtool.com.

Phil Herman Jr.
PH Tool


: Folks,
.
: I am wondering if anyone can reference me to information regarding surface preparation of an EDM cut aluminum surface that is to be penetrant inspected. My concerns are whether etching should be required or not, if so how aggressive of an etch, if not is there a different surface prep that is recommended. Does the EDM process have the tendency to smear metal, close pre-existing discontinuities, create new discontinuities?
.
: I am not familiar with the EDM process, therefore I have more questions than answers at this pointand would appreciate any input from anyone who does have some experience.
.
: Thanks in advance for your time,
.
: Brian Younce
: NDT Level III
: Hartzell Propeller Inc.
.



    
 
 Reply 
 
Sergio Bilbao
Sergio Bilbao
01:29 Oct-09-2002
Re: Pre-penetrant Surface Prep of an EDM Cut Aluminum Surface

Brian,

It depends on how your EDM Process in made.
For example, the roughness you are achieving. Anyway, EDM machined surfaces have a surface quality quite good.
If you are going to make a sensitivity 2 FP Inspection, it is probably you will get an acceptable background.

The EDM's most important characteristic is that it modifies the grain size in the subsurface layer, known as "Recast Layer". But it is not important for the FPI.

The EDM does not close discontinuities. And generally, doesn't create news indications.

Be care of oxidations and burns.

Regards.


: Folks,
.
: I am wondering if anyone can reference me to information regarding surface preparation of an EDM cut aluminum surface that is to be penetrant inspected. My concerns are whether etching should be required or not, if so how aggressive of an etch, if not is there a different surface prep that is recommended. Does the EDM process have the tendency to smear metal, close pre-existing discontinuities, create newdiscontinuities?
.
: I am not familiar with the EDM process, therefore I have more questions than answers at this point and would appreciate any input from anyone who does have some experience.
.
: Thanks in advance for your time,
.
: Brian Younce
: NDT Level III
: Hartzell Propeller Inc.
.



    
 
 Reply 
 

Product Spotlight

High-end Ultrasonic Flaw Detector with 32:128PR PAUT and 2-ch TOFD: SyncScan 2

SIUI’s newly launched SyncScan 2, is a high-end ultrasonic flaw detector with 32:128PR PAUT and
...
2-ch TOFD, which can maximize your efficiency for PA and TOFD. ● Support PA/TOFD/UT ● 32-ch PA is more suitable for inspection on extra-thick wall and high-attenuation material. ● 32-ch PA and 2-ch TOFD work simultaneously. ● Support PR mode for corrosion inspection.
>

PROlineTOP Plug & Play Ultrasonic inspection device

As Plug & Play solution it units all control and operation elements in a small housing and therefo
...
re replaces the typical control cabinet...
>

NDTkit RT

NDTkit RT, TESTIA's Digital Radiography software The NDTkit product line software for X-ray analysi
...
s. NDTkit RT is a software benefiting from the Ultis kernel which is dedicated to radiographic image analysis. It offers a set of tools and filtering processes to assist RT operators in finding relevant flaws.
>

CIVA 2017 UT Module

CIVA NDE Simulation Software is the world leader of NDT Simulation. The UT simulation Module incl
...
udes: - "Beam computation": Beam propagation simulation - "Inspection Simulation": Beam interaction with flaws or specimens The user can simulate a whole inspection process (pulse echo, tandem or TOFD) with a wide range of probes (conventional, Phased- arrays or EMAT), components, and flaws.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window