Cracking In Carbon Steel

Hello everyone,

All fabrication and inspection is to AWS D1.1. Fabricating utility poles that are tapered with 12 or 18 flats. 1/4-5/8 shaft and 2 1/2 to 4in. flange is the range of raw material as of now. Finding many cracks in weld. Specifically inspecting today a 7/16 in. shaft welded to 3 in. flange. Mig welding a single groove, 45 degree bevel. Welding inner pass first then coming outside and back gouging and laying multiple passes to obtain CJP. Welding parameters are: Wire- Hobart .052 and Lincoln .052, Wire speed- 330, Volts- 26.5, Gas- 90AR 10Co2. Pre-heat- 300 F of flange and shaft"at least 3in. from direct area being welded." Everyone has gotten involved including engineering and owners. Material certs have been checked as well as WPS's verified as ok for our application. Cannot find solution. Found multiple defects with height reading as 1/4 to 7/16. Welder arc gouged and did find cracks. Then ground to specified height reading and re-welded. No verification that defect was gone with any other NDT method. When I checked with UT same indication and identical characteristics on A-scan as first inspection but now 000"- 5/16. Welder arc-gouged in and indeed found cracks again even though welder claimed that all defects were gone when he began welding for the repair. I'm being questioned as the UT tech of whether or not I'm giving accurate measurements. Is it possible for cracks to propagate height wise through the volume of the weld and why are we having so much cracking in the first place?

 
 Reply 
 
Mark
,
Zambia, Joined Jun 2016, 49

Mark

,
Zambia,
Joined Jun 2016
49
07:54 Jul-03-2016
Re: Cracking In Carbon Steel
In Reply to John Lomax at 17:31 Jul-02-2016 (Opening).

John,
Can you upload any sketch of bevel configuration or WPS?

 
 Reply 
 
Heydar Alakbarov
NDT Inspector,
Inspection Services, Inc., USA, Joined May 2016, 8

Heydar Alakbarov

NDT Inspector,
Inspection Services, Inc.,
USA,
Joined May 2016
8
01:52 Jul-05-2016
Re: Cracking In Carbon Steel
In Reply to John Lomax at 17:31 Jul-02-2016 (Opening).

John,
I recommend to verify metal soundness after air gouging by using MT. Very often visually it looks like crack removed but when you apply MT you see reminded crack which expanded during rewelding.

 
 Reply 
 
John
NDT Inspector,
USA, Joined Jul 2016, 6

John

NDT Inspector,
USA,
Joined Jul 2016
6
13:03 Jul-05-2016
Re: Cracking In Carbon Steel
In Reply to Mark at 07:54 Jul-03-2016 .

zoom image



Hopefully you can see it.
 
 Reply 
 
Paul Holloway
Consultant,
Holloway NDT & Engineering Inc , Canada, Joined Apr 2010, 218

Paul Holloway

Consultant,
Holloway NDT & Engineering Inc ,
Canada,
Joined Apr 2010
218
17:32 Jul-05-2016
Re: Cracking In Carbon Steel
In Reply to John at 13:03 Jul-05-2016 .

Hi John,

Can you sketch exactly where the cracks are showing up? It's too bad you are being questioned as to your accuracy when upon excavation the cracks are visible. I've seen this happen alot and it's very frustrating... we're always the bearer of bad news!

-Paul

 
 Reply 
 
John
NDT Inspector,
USA, Joined Jul 2016, 6

John

NDT Inspector,
USA,
Joined Jul 2016
6
18:04 Jul-05-2016
Re: Cracking In Carbon Steel
In Reply to Paul Holloway at 17:32 Jul-05-2016 .

Hi Paul,

I would say 90% of the time it's between the inner pass and root pass. A lot of times I also find cracking on the knuckles where the weld profile is concave, in the scenario it's almost always center line cracking.


 
 Reply 
 
John
NDT Inspector,
USA, Joined Jul 2016, 6

John

NDT Inspector,
USA,
Joined Jul 2016
6
17:25 Jul-06-2016
Re: Cracking In Carbon Steel
In Reply to Paul Holloway at 17:32 Jul-05-2016 .

Hi Paul,

I would say 90% of the time it's between the inner pass and root pass. A lot of times I also find cracking on the knuckles where the weld profile is concave, in the scenario it's almost always center line cracking.


 
 Reply 
 

Product Spotlight

Wireless TOFD scanner

Quick, accurate and highly reproducible welds testing. The System operates wirelessly and is compat
...
ible with any type of Windows based Laptop, Desktop or Tablet.
>

FD800 Bench Top Flaw Detectors

The bench-top FD800 flaw detector range combines state-of-the-art flaw detection with advanced mater
...
ial thickness capabilities. Designed for use in the laboratory these gauges are the tool you need for all your flaw detecting needs.
>

Ultrasonic Testing Immersion Tanks with Unmatched Scanning Features

TecScan’s non-destructive testing Ultrasonic Immersion Tanks & scanners are designed for high pe
...
rformance and demanding NDT testing applications. Our Scan3D™ line of High Precision Immersion Tanks are specifically designed for automated ultrasonic testing of complex composites parts used in aerospace and industrial applications.
>

MIZ®-21C: Truly Affordable Eddy Current Handheld with Surface Array Capability

Introducing MIZ-21C, the first truly affordable handheld eddy current instrument with surface array
...
capabilities. MIZ-21C can deliver fast, accurate inspections in demanding NDT applications including aerospace, oil and gas, manufacturing, and power generation. The surface array solution can reduce inspection time by up to 95% compared to traditional handheld pencil probes. The ergonomic design, long battery life, and intuitive touchscreen mean you can inspect more areas faster than ever without fatigue.
>