Jim McGregor
Jim McGregor
01:23 Jun-02-2004
Attenuation measurments to check for hydrogen attack

I am looking for information on carrying out attenuation measurments on a 75mm thick carbon steel vessel before and after heat soak to check for hydrogen dispersement. The vessel has been in use for the past 10 years or so. Any help with details and /or a test procedure would be appreciated.

Thanks,

Jim McGregor


 
 Reply 
 
Sasaki
Sasaki
03:34 Jun-02-2004
Re: Attenuation measurments to check for hydrogen attack
There are five methods to detect a certain type of hydrogen attack:
1) flaw echo
2) attenuation
3) frequency analysis
4) sound velocity
5) comparison of longitudinal/transverse sound velocities


 
 Reply 
 
Kasper Pols
Kasper Pols
09:35 Jun-02-2004
Re: Attenuation measurments to check for hydrogen attack
----------- Start Original Message -----------
: I am looking for information on carrying out attenuation measurments on a 75mm thick carbon steel vessel before and after heat soak to check for hydrogen dispersement. The vessel has been in use for the past 10 years or so. Any help with details and /or a test procedure would be appreciated.
: Thanks,
: Jim McGregor
------------ End Original Message ------------

See website: Sensistor



 
 Reply 
 
Jan Verkooijen
Director,
Sonovation, Netherlands, Joined Nov 1998, 29

Jan Verkooijen

Director,
Sonovation,
Netherlands,
Joined Nov 1998
29
04:28 Jun-02-2004
Re: Attenuation measurments to check for hydrogen attack
----------- Start Original Message -----------
: : I am looking for information on carrying out attenuation measurments on a 75mm thick carbon steel vessel before and after heat soak to check for hydrogen dispersement. The vessel has been in use for the past 10 years or so. Any help with details and /or a test procedure would be appreciated.
: : Thanks,
: : Jim McGregor
: See website: Sensistor
------------ End Original Message ------------
Jim,

Detection and monitoring is not a simple subject.
First of all you have to define what type of Hydrogen damage can be expected. Is the vessel operating in high temperature / high pressure environment? In this case you could have High Temperature Hydrogen Attack. Is it working at low temperature, you might be looking at one or more types of Hydrogen Induced Cracking. There is not one method that on its own will give you a conclusive answer on whether you do or don't have Hydrogen Damage. Therefore, during the last 15 years we have developed and practiced combinations of techniques, optimised for the situation at hand. We provide the service worldwide, so if you are interested let us look at your challenge.

Best regards,

Jan Verkooijen



 
 Reply 
 

Product Spotlight

NDT.net launches mobile-friendly design

NDT.net has revamped its website providing a mobile-friendly design.The front page received a comp
...
letely new design and all other sections are now reacting responsively on mobile devices. This has been a major step to make our website more user- friendly.
>

High-performance Linear Phased Array Probes

Available to order from stock in a range of 5MHz – 7.5MHz and from 16 to 64 elements. Designed w
...
ith piezo-composite elements, Phoenix phased array probes provide high-resolution imaging to maximise sensitivity; accurate ultrasonic detection and sizing of defects in welds; and effective corrosion mapping. Housed in a rugged stainless steel case for on-site industrial NDT applications.
>

Eddy Current inspection : RotoETscan Rotating Head

The rotating head RotoETscan detects the presence of longitudinal surface or sub surface defects a
...
t high speed. The rotating head is often installed directly on the production line. It is generally dedicated to the control of long products such as tubes, bars and wires, made of ferrous or non-ferrous material. It can also be used for inspection of small parts (billets).
>

Sci Aps Z-Series Portable Handheld Analysers

The world’s only handheld analyzer that measures carbon content in stainless (yes even L-grades),s
...
teels, and cast irons. Also accepted for low Si analysis for sulfidic corrosion analysis, and is widely used in the power industry for Cr analysis, for flow accelerated corrosion applications.
>