where expertise comes together - since 1996 -

The Largest Open Access Portal of Nondestructive Testing (NDT)

Conference Proceedings, Articles, News, Exhibition, Forum, Network and more

where expertise comes together
- since 1996 -

Ultrasonic Sciences Ltd
We specialize in the design and manufacture of automated and semi-automated ultrasonic testing systems, including multi axis, multi channels systems and phased array electronics.
2514 views
Technical Discussions
S S Ananthan
Consultant,
RAA Tech Solutions, India, Joined Jun 2000, 36

S S Ananthan

Consultant,
RAA Tech Solutions,
India,
Joined Jun 2000
36
03:47 Jun-04-2004
NDT of oxidised root welds

Hello,

In RT of 9 % Cr 1 Mo welded tubes can we identify the root oxidation ? Has any one got the experience in the postive identification of the presence of oxidation ? Can it be identified by UT ?

Additioanlly has this oxidation any deleterious effect in the life of the weld ?

Any comments on this will be useful.

S S Ananthan


 
 Reply 
 
Floyd Atkinson
NDT Inspector
American Inspection Society, Inc., USA, Joined Jun 2004, 10

Floyd Atkinson

NDT Inspector
American Inspection Society, Inc.,
USA,
Joined Jun 2004
10
05:28 Jun-05-2004
Re: NDT of oxidised root welds
----------- Start Original Message -----------
: Hello,
: In RT of 9 % Cr 1 Mo welded tubes can we identify the root oxidation ? Has any one got the experience in the postive identification of the presence of oxidation ? Can it be identified by UT ?
: Additioanlly has this oxidation any deleterious effect in the life of the weld ?
: Any comments on this will be useful.
: S S Ananthan
------------ End Original Message ------------

I have prior PMI and RT experience and feel the oxidation varies to widely to utilize RT for evaluation of an errosive root to face welds.


First, your eyes do not deceive you. Red rust is red rust.Alternatively, a brushed non-contaminated surface sample could identify the root cause of the root deterioration.The random sample should be evaluated for chemical contaminants in controlled laboratory conditions. Remember, the water for circulation in the vessel may have had bromide added to it for heat transfer properties.

Possible causes:
1)This may bea materials dilution / cross contamination problem if it is red rust. Check out the welding fabrication of the welds.I had welders use a carbon steel contaminated power wheel wire brush to grind their welds. They were unknowningly cross contaminating their welds to carbon steel.Later their welds on the stainless steel vessels rusted in the rain.

2)If this problem is predominately throughout the welds, there may have been a welding wire chemical dilution problem during fabrication.Check the owners operators data package for that specific serial number vessel fabrication.Confirm the Welding procedure specification was adhered to during fabrication.The wire supplier and their materials test reports supplied by the vendor/fabricaton should be readily available for your evaluation.
The welds dilution may be evaluted by the PMI tests methods.However,the surface interface will have to be polished if accessible for the dry method PMI testing.


Optionally, Radiographic Testing as in RT will determine the density change in the welds profile as accessible.A step wedge is utilized for this testing evaluation using medical grade (Grade M) fine grain film.Be sure the geometric unsharpness standard is adhered to by your radiogapher. This means get a sharp image of the welds over the welds viewing areas on the film between the markers.Make sure the two "T" hole on the penny or all six wires are clearly visible on your RT film. This may require an RT tubed source since as it is thin walled tube to head plate and intermitent spacers welds as in boiler interfaces.

Further, Magnetic resonance testing may reveal other areas of trouble spots by professionals in those areas. This is called eddy current testing. If you want to go this method, I recommend Hellier and Associates. They train the eddy current operators.

Good luck in your search for the truth.


 
 Reply 
 
S.V.Swamy
Engineering, - Material Testing Inspection & Quality Control
Retired from Nuclear Fuel Complex , India, Joined Feb 2001, 787

S.V.Swamy

Engineering, - Material Testing Inspection & Quality Control
Retired from Nuclear Fuel Complex ,
India,
Joined Feb 2001
787
06:11 Jun-08-2004
Re: NDT of oxidised root welds
Dear Shri Ananathan,

Greetings. Are you talking of oxidation during welding (caused by inadequate shielding) or during service? It looks as if you are interested in detecting oxidation at the fabrication stage.

If the oxide deposits are really serious, they should be visible in RT, just like slag inclusions. UT may or may not detect them depending on the acoustic impedance mismatch. Best way is to create some oxidation and then try to detect the same.

Oxide at the root is like slag. So what will be the long term effect on service can be looked at from that aspect.

Best wishes.

Swamy

----------- Start Original Message -----------
: Hello,
: In RT of 9 % Cr 1 Mo welded tubes can we identify the root oxidation ? Has any one got the experience in the postive identification of the presence of oxidation ? Can it be identified by UT ?
: Additioanlly has this oxidation any deleterious effect in the life of the weld ?
: Any comments on this will be useful.
: S S Ananthan
------------ End Original Message ------------




 
 Reply 
 
NAT
NAT
01:25 Jun-14-2004
Re: NDT of oxidised root welds
----------- Start Original Message -----------
: Dear Shri Ananathan,
: Greetings. Are you talking of oxidation during welding (caused by inadequate shielding) or during service? It looks as if you are interested in detecting oxidation at the fabrication stage.
: If the oxide deposits are really serious, they should be visible in RT, just like slag inclusions. UT may or may not detect them depending on the acoustic impedance mismatch. Best way is to create some oxidation and then try to detect the same.
: Oxide at the root is like slag. So what will be the long term effect on service can be looked at from that aspect.
: Best wishes.
: Swamy
: : Hello,
: : In RT of 9 % Cr 1 Mo welded tubes can we identify the root oxidation ? Has any one got the experience in the postive identification of the presence of oxidation ? Can it be identified by UT ?
: : Additioanlly has this oxidation any deleterious effect in the life of the weld ?
: : Any comments on this will be useful.
: : SS Ananthan
------------ End Original Message ------------

Weld oxyidation is does not look like slag as slag is of darker density. Weld oxyidation is bit britter than the near by weld metal with cloudy ,sponge like apperance some times associated with small spatter like weld metal sticking to it.
When a molten weld is oxyidized itlosses its desired properties , weaks mechanical and chemical

The welds with oxyidation tested desturtively have not passed any root bend test in my experiance(WPS)

However as No code has particularly identifed it as repair so far.
it up to the manufacturer to decide, if possiable to repair it better repair it.




 
 Reply 
 
Gary Woodside
Gary Woodside
02:10 Jun-14-2004
Re: NDT of oxidised root welds
One of the easiest ways to see root oxidation is to use a camera.----------- Start Original Message -----------
: : Dear Shri Ananathan,
: : Greetings. Are you talking of oxidation during welding (caused by inadequate shielding) or during service? It looks as if you are interested in detecting oxidation at the fabrication stage.
: : If the oxide deposits are really serious, they should be visible in RT, just like slag inclusions. UT may or may not detect them depending on the acoustic impedance mismatch. Best way is to create some oxidation and then try to detect the same.
: : Oxide at the root is like slag. So what will be the long term effect on service can be looked at from that aspect.
: : Best wishes.
: : Swamy
: : : Hello,
: : : In RT of 9 % Cr 1 Mo welded tubes can we identify the root oxidation ? Has any one got the experience in the postive identification of the presence of oxidation ? Can it be identified by UT ?
: : : Additioanlly has this oxidation any deleterious effect in the life of the weld ?
: : : Any comments on this will be useful.
: : : S S Ananthan
: Weld oxyidation is does not look like slag as slag is of darker density. Weld oxyidation is bit britter than the near by weld metal with cloudy ,sponge like apperance some times associated with small spatter like weld metal sticking to it.
: When a molten weld is oxyidized itlosses its desired properties , weaks mechanical and chemical
: The welds with oxyidation tested desturtively have not passed any root bend test in my experiance(WPS)
: However as No code has particularly identifed it as repair so far.
: it up to the manufacturer to decide, if possiable to repair it better repair it.
:
------------ End Original Message ------------




 
 Reply 
 

Product Spotlight

Magnetic X-Ray Pipeline Crawler

Zhong Yi brand pipeline crawler is magnetic/micro-video controlled crawler with DC X ray unit inst
...
alled for checking welding of pipeline. Move steadily inside the pipeline 6''-60''diameter with speed of up to 18m/min, Max. moving diatance 5 kilometers and provide the efficient inspection of the pipeline.
>

Wireless TOFD scanner

Quick, accurate and highly reproducible welds testing. The System operates wirelessly and is compat
...
ible with any type of Windows based Laptop, Desktop or Tablet.
>

CIVA 2017 UT Module

CIVA NDE Simulation Software is the world leader of NDT Simulation. The UT simulation Module incl
...
udes: - "Beam computation": Beam propagation simulation - "Inspection Simulation": Beam interaction with flaws or specimens The user can simulate a whole inspection process (pulse echo, tandem or TOFD) with a wide range of probes (conventional, Phased- arrays or EMAT), components, and flaws.
>

Immersion systems

ScanMaster ultrasonic immersion systems are designed for high throughput, multi shift operation in a
...
n industrial or lab environment. These fully integrated systems provide various scanning configurations and incorporate conventional and phased arrays technologies to support diverse applications, such as inspection of disks, bars, shafts, billets and plates. All of ScanMaster immersion systems are built from high accuracy scanning frames allowing for scanning of complex parts and include a multi-channel ultrasonic instrument with exceptional performance. The systems are approved by all major manufacturers for C-scan inspection of jet engine forged discs. Together with a comprehensive set of software modules these flexible series of systems provide the customer with the best price performance solutions.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window