sandeep sharma
sandeep sharma
09:19 May-17-2005
even after carrying out the magnetic particle test 350 mm dia shaft failed

dear all,
i would be highly obeliged if you can throw the light on a failure of hollow shaft of o.d. 350 mm and id. 100 mm (moc 15Cr Ni Mo4) duly heat treated . Hollow portion is for cooling water (demineralized) to keep its temp down to get better tensile and tortional strength.
This shaft was a used shaft, operator was suspecting leakage so when it was replaced it was decided to test it for cracks by using magnetic particle test. In which this shaft was found O.K. even a hydro test was carried out upto the 35 bar again we could not found the leakage so it was decided to use the shaft.
But after commisioning the shaft it failed within 10 days and at the surface of the fracture there was rusting below the surface covering at least 50 % of area.
What possibly be the mistake made by our NDT people?
Kindly throw some light if you can.

Thanks


 
 Reply 
 
Frank Lund
R & D,
United Kingdom, Joined Apr 2005, 222

Frank Lund

R & D,
United Kingdom,
Joined Apr 2005
222
00:33 May-18-2005
Re: even after carrying out the magnetic particle test 350 mm dia shaft failed

The fact that leakage was suspected indicated a crack reaching to the surface. In many applications to find such defects the EMA technique has been very successful. ELF in Norway switched to EMA after seeing it find defects which were revealed by grinding but not by MPI.

----------- Start Original Message -----------
: dear all,
: i would be highly obeliged if you can throw the light on a failure of hollow shaft of o.d. 350 mm and id. 100 mm (moc 15Cr Ni Mo4) duly heat treated . Hollow portion is for cooling water (demineralized) to keep its temp down to get better tensile and tortional strength.
: This shaft was a used shaft, operator was suspecting leakage so when it was replaced it was decided to test it for cracks by using magnetic particle test. In which this shaft was found O.K. even a hydro test was carried out upto the 35 bar again we could not found the leakage so it was decided to use the shaft.
: But after commisioning the shaft it failed within 10 days and at the surface of the fracture there was rusting below the surface covering at least 50 % of area.
: What possibly be the mistake made by our NDT people?
: Kindly throw some light if you can.
: Thanks
------------ End Original Message ------------




 
 Reply 
 
Nick Welland
Other, Quality and NDT
Aben Technical Services, Australia, Joined Oct 1999, 42

Nick Welland

Other, Quality and NDT
Aben Technical Services,
Australia,
Joined Oct 1999
42
01:14 May-18-2005
Re: even after carrying out the magnetic particle test 350 mm dia shaft failed
----------- Start Original Message -----------
: dear all,
: i would be highly obeliged if you can throw the light on a failure of hollow shaft of o.d. 350 mm and id. 100 mm (moc 15Cr Ni Mo4) duly heat treated . Hollow portion is for cooling water (demineralized) to keep its temp down to get better tensile and tortional strength.
: This shaft was a used shaft, operator was suspecting leakage so when it was replaced it was decided to test it for cracks by using magnetic particle test. In which this shaft was found O.K. even a hydro test was carried out upto the 35 bar again we could not found the leakage so it was decided to use the shaft.
: But after commisioning the shaft it failed within 10 days and at the surface of the fracture there was rusting below the surface covering at least 50 % of area.
: What possibly be the mistake made by our NDT people?
: Kindly throw some light if you can.
: Thanks
------------ End Original Message ------------

1. Was the crack propagating fromthe OD or the bore?
2. Was it a circumferential crack? If so, did it coincide with a change in section, or evident surface marks?
3. Does the corrosion on the exposed fracture surface indicate the crack was through-wall around any part of the periphery?
4. What magnetizing method did the NDT techs use?

Best regards
Nick


 
 Reply 
 
S.R.G.PRABHU
S.R.G.PRABHU
01:53 May-18-2005
Re: even after carrying out the magnetic particle test 350 mm dia shaft failed

I always doubt the success of MPI, as either it is done in a hurried manner or the technique and technicians are not up to the standard.Why can't we switch to other latest methods?

----------- Start Original Message -----------
: dear all,
: i would be highly obeliged if you can throw the light on a failure of hollow shaft of o.d. 350 mm and id. 100 mm (moc 15Cr Ni Mo4) duly heat treated . Hollow portion is for cooling water (demineralized) to keep its temp down to get better tensile and tortional strength.
: This shaft was a used shaft, operator was suspecting leakage so when it was replaced it was decided to test it for cracks by using magnetic particle test. In which this shaft was found O.K. even a hydro test was carried out upto the 35 bar again we could not found the leakage so it was decided to use the shaft.
: But after commisioning the shaft it failed within 10 days and at the surface of the fracture there was rusting below the surface covering at least 50 % of area.
: What possibly be the mistake made by our NDT people?
: Kindly throw some light if you can.
: Thanks
------------ End Original Message ------------




 
 Reply 
 
Simon Amalraja
Simon Amalraja
04:04 May-24-2005
Re: even after carrying out the magnetic particle test 350 mm dia shaft failed
----------- Start Original Message -----------
: The fact that leakage was suspected indicated a crack reaching to the surface. In many applications to find such defects the EMA technique has been very successful. ELF in Norway switched to EMA after seeing it find defects which were revealed by grinding but not by MPI.
: : dear all,
: : i would be highly obeliged if you can throw the light on a failure of hollow shaft of o.d. 350 mm and id. 100 mm (moc 15Cr Ni Mo4) duly heat treated . Hollow portion is for cooling water (demineralized) to keep its temp down to get better tensile and tortional strength.
: : This shaft was a used shaft, operator was suspecting leakage so when it was replaced it was decided to test it for cracks by using magnetic particle test. In which this shaft was found O.K. even a hydro test was carried out upto the 35 bar again we could not found the leakage so it was decided to use the shaft.
: : But after commisioning the shaft it failed within 10 days and at the surface of the fracture there was rusting below the surface covering at least 50 % of area.
: : What possibly be the mistake made by our NDT people?
: : Kindly throw some light if you can.
: : Thanks
------------ End Original Message ------------

You can also try UT Leak Detection. You need to plug both ends and try to pressurise it and look for the leak by Leak Detectors of reputed makes.

If you are in India, contact me for further details.

D.Simon Amallraja.
Mobile: 09866343309.


 
 Reply 
 

Product Spotlight

IRIS 9000Plus - Introducing the next generation of heat exchanger inspection.

Representing the seventh generation of the IRIS system, the IRIS 9000 Plus has nearly 200 years of c
...
ombined field inspection experience incorporated in its design. This experience combined with a strong commitment to quality and a history of innovation has made Iris Inspection Services® the undisputed leader in IRIS technology.
>

OPBOX with standard software is able to do all types of inspections and measurements: flaw detection in welds and materials, scanning of objects, testing composite materials, forged and moulded pieces, many UT inspections, measurements of properties of ma

Typical applications: UT measurements with pulse technique, Measurement of thicknesses also at hig
...
h temperatures, Measurements of properties of materials, including fluids and gases We are delivering a standard version of the software (for any Microsoft Windows up to 10 x64 with Microsoft Hardware certification report Approved) and for special needs: SDK with ready to use examples for LabView, MATLAB x64, C++ wrapper for dll, Python and Linux., and also low-level description of how to control our devices directly from any USB tools
>

VeeScan AirCraft Wheel Inspection

The VEESCAN offers maximum flexibility, has a proven mechanical design and records of breakdown-fr
...
ee operation of over 365 days. Appealing to companies in the Aerospace industry, the VEESCAN is ideal for all wheel-testing environments. With a wide selection of probes, the VeeScan allows your wheel testing facility the flexibility to select the most compatible configurations with their workload.
>

PAUT Probes

Typical Phased Array probes have frequencies between 1MHz and 20MHz and the number of wafers is 10
...
to 128. M2 Electronics offers customers conventionally ultrasound probes and the ability to provide high-precision Phased Array Ultrasound Probes of up to 256 wafers. We can also customize the probe for our customers to meet the specific application requirements of the user.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window