00:39 Feb-09-2001
distinguishing flaws from martensite

Hello all, have a question for the forum, slightly off course from the other martenstie detection question in thin sheet...

I am looking at friction (inertia) welded, mild steel components. The joint line exhibits significant amounts of martensitic formation, which produce apparent pronounced ultrasonic indications; their presence was verified by metallography, while revealing the absence of flaw/disbond regions. Even after normalizing heat treatment, the indications were quite pronounced.

The question is, can we possibly expect to distinguish between such formations and true flaws? By flaws, I mean regions at the interface which did not fuse during the inertia welding process. It seems as if we won't be able to see through the microstructural reflections and find flaws. But based on other samples, the process is not fully under control, and such a lack of fusion does indeed occur on occasion.

My kind thanks to any responses,
Dave Utrata


 
 Reply 
 
Dent McIntyre
Consultant, NDE Manager NDELevel III/3
NDT Consultant, Canada, Joined Nov 1998, 250

Dent McIntyre

Consultant, NDE Manager NDELevel III/3
NDT Consultant,
Canada,
Joined Nov 1998
250
01:06 Feb-09-2001
Re: distinguishing flaws from martensite
: Hello all, have a question for the forum, slightly off course from the other martenstie detection question in thin sheet...
.
: I am looking at friction (inertia) welded, mild steel components. The joint line exhibits significant amounts of martensitic formation, which produce apparent pronounced ultrasonic indications; their presence was verified by metallography, while revealing the absence of flaw/disbond regions. Even after normalizing heat treatment, the indications were quite pronounced.
.
: The question is, can we possibly expect to distinguish between such formations and true flaws? By flaws, I mean regions at the interface which did not fuse during the inertia welding process. It seems as if we won't be able to see through the microstructural reflections and find flaws. But based on other samples, the process is not fully under control, and such a lack of fusion does indeed occur on occasion.
.
: My kind thanks to any responses,
: Dave Utrata


Dave:
Ever try to send sound through 2 Jo blocks that have been wrung together? Try it.

What you get is sound goes right through with little loss and little relection. This is what LOF will show like on these welds.

Been there done that 20 years ago. Has anything changed since then to make it any better? I do not think so. If there is I am all ears.

Dent


 
 Reply 
 
M. W. Moyer
M. W. Moyer
02:28 Feb-09-2001
Re: distinguishing flaws from martensite
You don't even need gage blocks. I once set up two blocks under compressive load. The amplitude of the reflection was inversely proportional
to the load. At yield, the reflection was essentially zero. When I unloaded the system the blocks fell apart. What happens is at zero load,
only a few high points touch. As the load increases, the high point yield and more of the area is in contact until at yield the whole surface
is in contact. Since the sound wave has a very low pressure amplitude (a few psi) compared with the load, the wave is transmitted through the
interface with little or no reflection.

When ever you have an interface that is under a compressive load sound can easily travel through the interface. We have seen this condition in
partially penetrated welds. We got no reflection from the unwelded interface below the weld because it was under compression. Eddy current inspections
can suffer from the same problem.

M. W. Moyer


: Dave:
: Ever try to send sound through 2 Jo blocks that have been wrung together? Try it.
.
: What you get is sound goes right through with little loss and little relection. This is what LOF will show like on these welds.
.
: Been there done that 20 years ago. Has anything changed since then to make it any better? I do not think so. If there is I am all ears.
.
: Dent
.



 
 Reply 
 
Ricardo Ortiz Alcantar
Ricardo Ortiz Alcantar
09:30 Aug-29-1998
Asking for information about a especiality or a master degree about presstressing
Hello,
I am from Guadalajara, Jalisco MEXICO, i am civil engineering, and i am looking to study about prestressing at some university or instute in USA or in Europe (Spain, France ), so i would like to know about it, and if you know some school in this speciality please let me know.

Gracias
Ricardo Ortiz



 
 Reply 
 
Leslie Chong
Leslie Chong
00:54 Dec-20-1999
Re: Asking for information about a especiality or a master degree about presstressing
: Hello,
Pls tell me about the methods of prestressing
Thank you



 
 Reply 
 

Product Spotlight

A1525 SOLO

A1525 Solo – the most compact and affordable TMF unit with two phased array transducers and 3D v
...
isualization and analysis software in standard delivery set. A compact, ergonomic and easy to handheld Phased Array unit based on Total Focusing Method for easy-going imaging of inspection objects with two-dimensional and three-dimensional visualization and evaluation of inspection results.
>

ISONIC 3510

Very Powerful Superior Performance Extremely Portable Smart Phased Array Ultrasonic Flaw Detector an
...
d Recorder with 2 Conventional UT and TOFD Channels uniquely combines PA, single- and multi-channel conventional UT, and TOFD modalities providing 100% raw data recording and imaging. Suitable for all kinds of every-day ultrasonic inspections
>

Research and Applications Development For NDT

The Research and Applications Development (RAD) group is a newly formed team within Acuren dedicat
...
ed to tackling challenging inspection problems. Our focus is the development of novel, field deployable, advanced inspection techniques for use in cases where standard NDT methods are ineffective. We don't wait for new innovations, we engineer them. From concept to commissioning.
>

Ultrasonic Squirter/Gantry System

TecScan’s NDT Ultrasonic Gantry Systems are industrial Squirter scanners designed for non-destru
...
ctive quality testing and raster scanning of large structures and parts. The Gantry Systems are usually composed of an Industrial Mechanical Scanner and a Control Room with System Workstation.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window