Looking for root erosion in thin-walled duplex stainless steel welds

We have air coolers on our plant (oil & gas) part of which consists of a row of 1 inch dia, 1,6 mm to 3,5 mm wall thickness duplex (22% Cr, UNS31803) tubes TIG welded with matching filler metal to an 8 inch duplex header (wt 11 - 18mm). Weld ferrite content range 35% - 65%.

I am no corrosion engineer but it seems that duplex is susceptible to weld root erosion or cracking in case of wet-upset in an H2S environment. So we wish to check the weld roots for such whilst new equipment fabricated from material more-suited to the potential environment are procured.

A simulation test rig of one header with 4 or 5 tubes welded in place is being made for performance demonstration purposes. Do anybody have experience of such configurations? Is low-frequency eddy current a possibility? Or DC MPI - knowing that the permeability variations may produce non-relevant indications. As the material/configuration set-up is difficult to inspect I expect signal interpretation and evaluation will be a problem. Any ideas?


 
 Reply 
 
Sayed H. El-Nekhaly
R & D
Delta Steel Mill Company, Egypt, Joined Jun 2006, 7

Sayed H. El-Nekhaly

R & D
Delta Steel Mill Company,
Egypt,
Joined Jun 2006
7
05:52 Oct-20-2006
Re: Looking for root erosion in thin-walled duplex stainless steel welds
This type of corrosion known as intergranular corrosion. It result due to depletion of chromium to be concentrated on grain boundaries during welding of high chromium stailess steel. Traces of nitrogen within range (0.1 - 0.5%) added as alloying element in duplex stainless steel can prevent this type of corrosion. The mechanism occured by catching chromium as chromium nitrid which prevent depletion then corrosion cracking.


 
 Reply 
 

Product Spotlight

UCI Hardness Tester NOVOTEST T-U2

UCI hardness tester NOVOTEST T-U2 is is used for non-destructive hardness testing of: metals and
...
alloys by scales of hardness: Rockwell (HRC), Brinell (HB), Vickers (HV); non-ferrous metals, alloys of iron etc., and using five additional scales for calibration; with tensile strength (Rm) scale determines the tensile strength of carbon steel pearlitic products by automatic recalculation from Brinell (HB) hardness scale.
>

On-Demand Webinar: Advanced Ultrasonic Techniques for HTHA Detection & Assessment

In the Oil and Gas industry, High Temperature Hydrogen Attack (HTHA) can occur in steels operating a
...
t high temperature, usually above 205°C (400°F). Early stages of HTHA are very difficult to detect. Join us for a webinar presented by Guy Maes, Zetec Sales Engineer Director. The webinar will demonstrate how advanced ultrasonic techniques are deployed for efficient and reliable HTHA inspections.
>

Ultrasonic Squirter/Gantry System

TecScan’s NDT Ultrasonic Gantry Systems are industrial Squirter scanners designed for non-destru
...
ctive quality testing and raster scanning of large structures and parts. The Gantry Systems are usually composed of an Industrial Mechanical Scanner and a Control Room with System Workstation.
>

OmniScan™ X3 flaw detector

The OmniScan X3 flaw detector is a complete phased array toolbox. Powerful tools, like total focus
...
ing method (TFM) images and advanced visualization capabilities, enable you to complete your inspection with greater confidence.
>

Share...
We use technical and analytics cookies to ensure that we will give you the best experience of our website - More Info
Accept
top
this is debug window